Fainplast Compounds GS 65/R-AS Flexible PVC, Injection Molding for Footwear
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded |
| Manufacturer | Fainplast Compounds |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fainplast Compounds GS 65/R-AS Flexible PVC, Injection Molding for Footwear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Oil resistent and antistatic soles
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 - 1.17 g/cc | 0.0408 - 0.0423 lb/in³ | ISO R 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 58 - 62 | 58 - 62 | ISO R 868 |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
| Elongation at Break | 300 % | 300 % | ISO R 527 |
| Abrasion | 100 | 100 | [mm³]; DIN 53516 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -60.0 °C | -76.0 °F | Cold Flex; ISO 458/2 |
Users viewing this material also viewed the following:
- MV Labs NI800 NiO Nickel(II) oxide
- PolyOne Edgetek® XT XT-100-BU01-HF Polycarbonate + PBT (PC+PBT)
- BASF Capron® SEG6 H1 30% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8127 PEEK, lubricant modified
- Teijin Panlite® LN-1250G Flame Resistant, Translucent Polycarbonate Resin
- A. Schulman POLYBATCH™ Beige 60199 Concentrate Based In LLDPE
- Chevron Phillips 1018 Extrusion Coating Resin
- Braskem TR3350CW Random Copolymer Polypropylene
- SABIC Innovative Plastics Noryl EN212 PPE+PS
Copyright © lookpolymers.com All Rights Reserved