- FKuR Kunststoff Biograde® C 7500 Biodegradable Plastic Compound
FKuR Kunststoff Biograde® C 7500 Biodegradable Plastic Compound
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Wood and Natural Products |
| Manufacturer | FKuR Kunststoff GmbH |
| Trade Name | Biograde® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | FKuR Kunststoff Biograde® C 7500 Biodegradable Plastic Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BIOGRADE® are easy to process blends based on cellulose. BIOGRADE® is composed mainly of natural resources. Based on cellulose, a product of the paper industry BIOGRADE® has been especially designed for injection molding applications. BIOGRADE® is mainly composed of natural resource materials (European Soft Wood from sustainable forestry) and does not contain starch or starch derivatives.Information Provided by FKuR Kunststoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.760 g/cc | 0.0275 lb/in³ | ISO 60 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Melt Flow | 17 - 21 g/10 min @Load 5.00 kg, Temperature 230 °C |
17 - 21 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 |
| Tensile Strength | 66.0 MPa | 9570 psi | ISO 527 |
| Elongation at Break | 12.5 % | 12.5 % | ISO 527 |
| Elongation at Yield | 12.5 % | 12.5 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | at 3.5% strain;; ISO 178 |
| Flexural Modulus | 2.95 GPa | 428 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1/1eU |
| Charpy Impact, Notched | 0.650 J/cm² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | >= 180 °C | >= 356 °F | ISO 3146-C |
| Vicat Softening Point | 110 °C | 230 °F | A; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Melt Volume Flow (cm3/10 min) | 9-13 | ISO 1133; 230°C, 5kg |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 80-7353/NAT Polyacetal-copolymer, with aramid reinforcement and PTFE
- ICO Polymers ICORENEâ„¢ 110-1327 LMDPE Rotational Molding Resin
- Chase Plastics CP Pryme® AC125G Acetal Copolymer, 25% Glass Fiber Reinforced
- Hexcel® HexForce™ 388 Aramid Fabric
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 0 PHR Tricresyl Phosphate
- EMS-Grivory Grivory® XE 4107 nat PA612-GF40
- BASF Ultramid® A3X2G5 BK 23185 25% Glass Filled PA66 FR (Conditioned)
- 3M 7965MP High Performance Adhesive Transfer Tapes with Adhesive 200MP
- DSM Akulon® F232-DH Nylon 6 (European Grade) (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved