FKuR Kunststoff Biograde® C 6530 Biodegradable Plastic Compound

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Wood and Natural Products
Manufacturer FKuR Kunststoff GmbH
Trade Name Biograde®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF FKuR Kunststoff Biograde® C 6530 Biodegradable Plastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BIOGRADE® are easy to process blends based on cellulose. BIOGRADE® is composed mainly of natural resources. Based on cellulose, a product of the paper industry BIOGRADE® has been especially designed for injection molding applications. BIOGRADE® is mainly composed of natural resource materials (European Soft Wood from sustainable forestry) and does not contain starch or starch derivatives. Furthermore BIOGRADE® has the following advantages: high content of natural resource materials excellent heat resistance - up to 115 °C injection mouldable on conventional injection moulding equipment processable with multi-cavity moulds flat sheet / film suitable for thermoforming on conventional deep drawing machinery properties comparable to polystyrene: rigid and transparent depending on grade. Food contact approved Biodegradability certified by independent organisations.BIOGRADE® C 6530 is a consitent further development of BIOGRADE® C 9550. BIOGRADE® C 6530 is especially suitable for the production of injection moulded rigid parts and those with thin walls and long flow paths. This optimization are possible through the appropriate and unique combination of additives and natural fillers. Thereby it features similar characteristics as BIOGRADE® C 9550. Information Provided by FKuR Kunststoff GmbH
Physical Properties Metric English Comments
Bulk Density 0.890 g/cc
0.0322 lb/in³
ISO 60
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
Melt Flow 27 - 31 g/10 min

@Load 5.00 kg,
Temperature 230 °C
27 - 31 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 44.0 MPa
6380 psi
At break; ISO 527
Tensile Strength, Yield 46.0 MPa
6670 psi
ISO 527
Elongation at Break 5.5 %
5.5 %
ISO 527
Elongation at Yield 9.0 %
9.0 %
ISO 527
Tensile Modulus 3.15 GPa
457 ksi
ISO 527
Flexural Yield Strength 58.0 MPa

@Strain 3.50 %
8410 psi

@Strain 3.50 %
ISO 178
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Charpy Impact Unnotched 3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1/1eU
Charpy Impact, Notched 0.350 J/cm²

@Temperature 23.0 °C
1.67 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1/1eA
Thermal Properties Metric English Comments
Melting Point >= 180 °C
>= 356 °F
ISO 3146-C
Vicat Softening Point 107 °C
225 °F
A; ISO 306
Descriptive Properties Value Comments
Flexural strain at break (%) No break
ISO 178
Melt Volume Flow (cm3/10 min) 20.5-23.5
ISO 1133; 230°C, 5kg