Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Fabric Form

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Fabric Form.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fibers: T300-3K, AS4C-3KInformation provided by HexCel
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
Laminate
Volatiles <= 2.0 %
<= 2.0 %
Prepreg
Mechanical Properties Metric English Comments
Tensile Strength, Yield 744 MPa

@Temperature 23.0 °C
 108000 psi

@Temperature 73.4 °F
 T300; Fill Tension; (AMB)
841 MPa

@Temperature 23.0 °C
 122000 psi

@Temperature 73.4 °F
 AS4C; Fill Tension; (AMB)
Tensile Modulus 55.8 GPa

@Temperature 23.0 °C
 8090 ksi

@Temperature 73.4 °F
56.3 GPa

@Temperature 23.0 °C
 8170 ksi

@Temperature 73.4 °F
Flexural Yield Strength 520 MPa

@Temperature 177 °C
 75400 psi

@Temperature 351 °F
 AS4C; Fill Flexure; Wet condition
552 MPa

@Temperature 177 °C
 80100 psi

@Temperature 351 °F
 T300; Fill Flexure; Wet condition
710 MPa

@Temperature 232 °C
 103000 psi

@Temperature 450 °F
 AS4C; Fill Flexure;
758 MPa

@Temperature 232 °C
 110000 psi

@Temperature 450 °F
 T300; Fill Flexure; AMB
917 MPa

@Temperature 23.0 °C
 133000 psi

@Temperature 73.4 °F
1041 MPa

@Temperature 23.0 °C
 151000 psi

@Temperature 73.4 °F
Flexural Modulus 51.3 GPa

@Temperature 177 °C
 7440 ksi

@Temperature 351 °F
 T300; Fill Flexure; Wet condition
52.0 GPa

@Temperature 177 °C
 7540 ksi

@Temperature 351 °F
 AS4C; Fill Flexure; Wet condition
54.0 GPa

@Temperature 232 °C
 7830 ksi

@Temperature 450 °F
 T300; Fill Flexure; AMB
54.0 GPa

@Temperature 232 °C
 7830 ksi

@Temperature 450 °F
 AS4C; Fill Flexure;
56.8 GPa

@Temperature 23.0 °C
 8240 ksi

@Temperature 73.4 °F
57.0 GPa

@Temperature 23.0 °C
 8270 ksi

@Temperature 73.4 °F
Compressive Yield Strength 408 MPa

@Temperature 177 °C
 59200 psi

@Temperature 351 °F
 AS4C; Fill Compression; Wet condition
438 MPa

@Temperature 177 °C
 63500 psi

@Temperature 351 °F
 T300; Fill Compression; Wet condition
510 MPa

@Temperature 232 °C
 74000 psi

@Temperature 450 °F
 T300; Fill Compression; AMB
531 MPa

@Temperature 232 °C
 77000 psi

@Temperature 450 °F
 AS4C; Fill Compression;
786 MPa

@Temperature 23.0 °C
 114000 psi

@Temperature 73.4 °F
889 MPa

@Temperature 23.0 °C
 129000 psi

@Temperature 73.4 °F
Compressive Modulus 8.18 GPa

@Temperature 177 °C
 1190 ksi

@Temperature 351 °F
 T300; Fill Compression; Wet condition
8.40 GPa

@Temperature 23.0 °C
 1220 ksi

@Temperature 73.4 °F
Shear Modulus 1.40 GPa

@Temperature 177 °C
 203 ksi

@Temperature 351 °F
 T300; In Plane; Wet condition
1.60 GPa

@Temperature 177 °C
 232 ksi

@Temperature 351 °F
 AS4C; In Plane; Wet condition
2.70 GPa

@Temperature 232 °C
 392 ksi

@Temperature 450 °F
 T300; In Plane; AMB
2.70 GPa

@Temperature 232 °C
 392 ksi

@Temperature 450 °F
 AS4C; In Plane
4.50 GPa

@Temperature 23.0 °C
 653 ksi

@Temperature 73.4 °F
4.50 GPa

@Temperature 23.0 °C
 653 ksi

@Temperature 73.4 °F
Shear Strength 34.0 MPa

@Temperature 177 °C
 4930 psi

@Temperature 351 °F
 AS4C; Fill Short Beam; Wet condition
39.0 MPa

@Temperature 177 °C
 5660 psi

@Temperature 351 °F
 T300; Fill Short Beam; Wet condition
50.0 MPa

@Temperature 232 °C
 7250 psi

@Temperature 450 °F
 AS4C; Fill Short Beam
54.0 MPa

@Temperature 232 °C
 7830 psi

@Temperature 450 °F
 T300; Fill Short Beam; AMB
67.0 MPa

@Temperature 232 °C
 9720 psi

@Temperature 450 °F
 AS4C; In Plane
68.0 MPa

@Temperature 23.0 °C
 9860 psi

@Temperature 73.4 °F
70.0 MPa

@Temperature 232 °C
 10200 psi

@Temperature 450 °F
 T300; In Plane; AMB
70.0 MPa

@Temperature 177 °C
 10200 psi

@Temperature 351 °F
 AS4C; In Plane; Wet condition
79.0 MPa

@Temperature 177 °C
 11500 psi

@Temperature 351 °F
 T300; In Plane; Wet condition
103 MPa

@Temperature 23.0 °C
 14900 psi

@Temperature 73.4 °F
120 MPa

@Temperature 23.0 °C
 17400 psi

@Temperature 73.4 °F
133 MPa

@Temperature 23.0 °C
 19300 psi

@Temperature 73.4 °F
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.0212
Laminate
Dry Resin Content (%) 40
Prepreg
Fiber Volume (%) 51
Laminate