ExxonMobil OPTEMA™ TC 140 Molding, extrusion, compounding and adhesive resin (discontinued **)

Category	Polymer , Adhesive , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil OPTEMA™ TC 140 Molding, extrusion, compounding and adhesive resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

OPTEMA TC 140 is a high flow, 21.5% methyl acrylate copolymer, which can be used in specialty applications such as a carrier for color and additive master batches, a compatibilizer in polymer compounds and hot melt adhesives. It can been processed at temperatures as low as 200°F and up to 600°F.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	ExxonMobil Method
Methyl Acrylate Content	21.5 %	21.5 %
Melt Flow	135 g/10 min	135 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	77	77	15s; ASTM D2240
Hardness, Shore D	21	21	15s; ASTM D2240
Tensile Strength at Break	2.83 MPa	410 psi	ASTM D638
Elongation at Break	575 %	575 %	ASTM D638
Flexural Modulus	0.0217 GPa	3.15 ksi	1% secant; ASTM D790
Impact Test	9.49 J @Temperature 23.0 °C	7.00 ft-lb @Temperature 73.4 °F	Instrument Impact, Total Energy; ASTM D3763
	16.3 J @Temperature -40.0 °C	12.0 ft-lb @Temperature -40.0 °F	Instrumented Impact, Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	74.4 °C	166 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	37.2 °C	99.0 °F	ASTM D1525

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer