SABIC Innovative Plastics LNP THERMOCOMP ZX06323 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZX06323 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This material is mineral filled PPO grade with high dielectric constant and low loss tangent
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.95 g/cc | 0.0704 lb/in³ | ASTM D792 |
| 1.95 g/cc | 0.0704 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0064 cm/cm @Time 86400 sec |
0.0064 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0056 cm/cm @Time 86400 sec |
0.0056 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 300 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
| 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D638 |
| 4.7 % | 4.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.08 GPa | 592 ksi | 1 mm/min; ISO 527 |
| 4.14 GPa | 600 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 102 MPa | 14800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 102 MPa | 14800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.94 GPa | 571 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.39 GPa | 637 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.460 J/cm | 0.862 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.94 J/cm | 5.51 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 6.4 @Frequency 9.00e+8 Hz |
6.4 @Frequency 9.00e+8 Hz |
ASTM D2520 - Mth B |
| Dissipation Factor | 0.0030 @Frequency 9.00e+8 Hz |
0.0030 @Frequency 9.00e+8 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- DuPont™ Surlyn® 8527 Ionomer Resin, Sodium (discontinued **)
- Lehmann & Voss LUVOCOM® 19/XCF/20 Polyamide 46, with carbon fiber
- ICE Al2O3 99.8
- Taiwan Sheen Soon Sheenthane® A8960N Thermoplastic Polyurethane Elastomer
- Techmer ES HiFill FR® PA6/6 GF25 FR-N IM3 BK 25% Glass Filled
- Unipetrol Grade B Diesel Oil
- ChevronTexaco EDM Fluid
- Cytec EN-14 (Conap) Casting, Potting, and Molding Compound
- BASF Ultramid® BG50XFI PA6 (Dry)
- Multibase Dow Corning® MB50-314 Siloxane Additive
Copyright © lookpolymers.com All Rights Reserved