ExxonMobil OPPalyte® 310 HSTW OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | OPPalyte® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil OPPalyte® 310 HSTW OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: One-side coated, white opaque OPP film with a proprietary cavitated core. It is designed for use unsupported or in a lamination for cold seal packaging applications. One side is treated.Availability: Latin America, North America and South AmericaKey Features:Treated surface provides excellent print qualityExcellent cold seal adhesionOutstanding flavor and aroma barrierVery good moisture barrierVery good moisture barrierGood oxygen barrierBright white appearanceFeatures: Flavor & Aroma BarrierGas BarrierHigh Barrier Printable PVdC CoatedHigh Barrier PvdC CoatedIn Lamination Lap SealableLight BarrierMoisture BarrierOxygen BarrierPVdC CoatedApplications: Confectionery, Chocolate Confectionery, Gum Confectionery, Sugar Uses:HFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 4.00 g/m²/day | 0.258 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 14.0 cc/m²/day | 0.902 cc/100 in²/day | 23°C, 0% RH; ExxonMobil Method |
| Thickness | 38.1 microns | 1.50 mil | ExxonMobil Method |
| Coating Weight | 21.6 g/m² | 13.5 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.53 | 0.53 | ExxonMobil Method |
| Film Tensile Strength at Break, MD | 77.911 MPa | 11300 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 138 MPa | 20000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % | 5.0 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 5.0 % | 5.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 90 % | 90 % | 45°; ExxonMobil Method |
| Transmission, Visible | 27 % | 27 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Wetting Tension | 0.8 receding COS theta | Treated Surface |
| Yield | 32100 in2/lb |
Users viewing this material also viewed the following:
- Resinlab® EP1390 Medium Viscosity, Self Extinguishing Flame Retardant Epoxy Casting Resin System
- Solvay Specialty Polymers Solef® 32008 PVDF Copolymer (Unverified Data**)
- LyondellBasell Astryn BA16G Polypropylene Copolymer
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Non-Black Sulfur Cure
- Aremco Corr-Paint™ CP2010 High Temperature Protective Coating Urethane, Aluminum Filled
- Colorite Polymers 4012 Clear Injection Molding Vinyl Compound
- Asahi Kasei Xyron® AT610 Modified Polyphenylene Ether
- Gwent Electronic Materials C2000802P2 Carbon Graphite Ink
Copyright © lookpolymers.com All Rights Reserved