ExxonMobil Label-Lyte™ 17LL222 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 17LL222 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: An uncoated biaxially oriented, transparent polypropylene film designed for overlamination in labeling applications where high gloss and high transparency are required.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Superb gloss and transparencyVery good printability and receptivity to laminating adhesivesGood tear and split resistanceGood mold resistanceExcellent machine performance Applications:Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral WatersBiscuits/Cookie/Crackers Dairy ProductsHealth and Beauty CareHousehold and DetergentsIndustrial Uses: Pressure Sensitive LabelsReel-Fed LabelsProcessing Method: Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, UV Flexographic Printing and UV Offset Lithography PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 17.0 microns | 0.670 mil | ExxonMobil Method |
| Coating Weight | 15.2 g/m² | 9.50 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 205 % | 205 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.50 GPa | 508 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.30 | 0.30 | ExxonMobil Method |
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.7 % | 1.7 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Yield | 45400 in2/lb |
Users viewing this material also viewed the following:
- Nylene® 609 Nylon 6, Film/Extrusion Grade
- Nitriflex SB-1011G Styrene Butadiene Copolymer
- Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA) (Unverified Data**)
- SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 5 PHR Di-Cup 40C
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR Di-Cup 40C Peroxide
- Ensinger Hydel® PEI-7 Polyetherimide (PEI), Static Dissipative
- BASF Neopor® 5300 Plus Expandable Polystyrene
- Eurotec® Tecomid® NB50 BK001 IH PA6, impact modified, black, extrusion grade
- BASF Myristyl Chloroformate
Copyright © lookpolymers.com All Rights Reserved