ExxonMobil LDPE LD 306.57 Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LDPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LDPE LD 306.57 Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LD 306 resins are 5.5% vinyl acetate copolymer, high clarity film resins. Film made from these resins exhibit superior impact strength and heat sealability.Availability: Latin America, North America and South America Additive: Antiblock: 4000 ppmSlip: No Thermal Stabilizer: YesApplications: Coextrusion FilmsFoamsForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmLamination FilmPoultry BagProduce BagsRice BagsInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil method |
| Vinyl Acetate Content | 5.5 % | 5.5 % | ExxonMobil Method |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Antiblock Level | 4000 ppm | 4000 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 |
| Film Elongation at Break, TD | 590 % | 590 % | ASTM D882 |
| Puncture Energy | 1.36 J | 1.00 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 80 g | 80 g | ASTM D1922 |
| Dart Drop Test | 170 g | 0.375 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 248 MPa | 36000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.1 MPa | 3500 psi | ASTM D882 |
| 1% Secant Modulus, MD | 124 MPa | 18000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 145 MPa | 21000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 216 °C | <= 421 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 74 % | 74 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 11 lbf | ExxonMobil Method |
Users viewing this material also viewed the following:
- Nye Lubricants 415 (SO) Synthetic Oil
- Pacific Sintered Materials FC-203-N Copper Iron Powdered Metal
- Eastman E6838-969F Polyethylene (discontinued **)
- Greene Tweed Fluoroelastomer 742 FKM
- Mearthane Durethaneâ„¢ S DS-285A Solid Polyurethane Elastomer
- Master Bond X-5 Elastomer Based, One Component Adhesive
- Westlake Tymax™ GT4157 Anhydride Modified Linear Low Density Polyethylene
- ChevronTexaco Dura-Lith® NLGI 0 Grease EP
- PolyOne Synprene® RT-3890MS Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved