Ashley Polymers Ashlene® 78MGS Nylon 6, 40% Glass Mineral reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 78MGS Nylon 6, 40% Glass Mineral reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A 40% glass mineral reinforced Nylon 6 with good dimensional stability, stiffness, sink and warp resistance.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Water Absorption | 0.090 % | 0.090 % | 24 hrs; ASTM D570 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ASTM D570 |
| Water Absorption at Saturation | 4.0 % | 4.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ATSM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 13.4 kV/mm | 340 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Quantum Composites QC-7810 55% Glass Fiber Polyester SMC (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7741 PEEK, with mineral filler, lubricant modified
- Global GPP-130-C 30% Glass Filled Chemically Coupled Polypropylene
- Sharadaa Ceramics ZAP 008 Smart Cast Application
- Teknor Apex Sinpolene MBB006LE Low Density Polyethylene
- Total MDPE HL 323 Medium Density Polyethylene, Film Resin
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/40%/285T2/AS4C-6K
- A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene
- Eurotec® Tecomid® MB40 GR20 NL PA6, 20% glass fiber reinforced, natural
- Ashley Polymers Ashlene® 626SB Nylon 6 Copolymer
Copyright © lookpolymers.com All Rights Reserved