ExxonMobil LD 143.26 High Clarity Packaging Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 143.26 High Clarity Packaging Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 143.26 is a homopolymer packaging film resin with excellent clarity and good stiffness. It is suitable for processing in either blown or cast film equipment. In blown film equipment LD 143.26 resin can be drawn down to 1.0 mil.Availability: Latin America, North America and South America Additive: Antiblock: 1500 ppmSlip: 750 ppmThermal Stabilizer: YesApplications: Blend PartnerCast FilmDisplay Packaging FilmFood PackagingForm Fill and Seal PackagingHigh Clarity FilmLamination FilmLight Duty Shrink FilmMail BagProduce BagsTextile Packaging Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	2.1 g/10 min @Load 2.16 kg, Temperature 190 °C	2.1 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	1500 ppm	1500 ppm
Slip Level	750 ppm	750 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.0 MPa	1600 psi	ASTM D882
Film Elongation at Break, MD	190 %	190 %	ASTM D882
Film Elongation at Break, TD	550 %	550 %	ASTM D882
Puncture Energy	0.463 J	0.342 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	380 g	380 g	ASTM D1922
Elmendorf Tear Strength TD	160 g	160 g	ASTM D1922
Dart Drop Test	80.0 g	0.176 lb	ASTM D1709
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ASTM D882
1% Secant Modulus, MD	207 MPa	30000 psi	ASTM D882
1% Secant Modulus, TD	248 MPa	36000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	111 °C	232 °F	Peak Melting Temperature; ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	6.2 %	6.2 %	ASTM D1003
Gloss	72 %	72 %	45°; ASTM D2457
Transmission, Visible	90 %	90 %	clear; thickness not quantified

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer