ExxonMobil LD 124.MS General Purpose Clarity Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 124.MS General Purpose Clarity Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 124.MS blown film resin offers an excellent balance of optical and strength properties for general purpose clear film applications. Availability: Latin America, North America and South America Additive: Antiblock: 2000 ppmSlip: 400 ppmThermal Stabilizer: YesApplications: Blend PartnerFood PackagingForm Fill and Seal PackagingHigh Clarity FilmLamination FilmLight Duty Shrink FilmMail BagProduce BagsTextile Packaging Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 2.1 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.1 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 2000 ppm
2000 ppm
Slip Level 400 ppm
400 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 12.4 MPa
1800 psi
ASTM D882
Film Elongation at Break, MD 130 %
130 %
ASTM D882
Film Elongation at Break, TD 540 %
540 %
ASTM D882
Puncture Energy 0.362 J
0.267 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 580 g
580 g
ASTM D1922
Elmendorf Tear Strength TD 110 g
110 g
ASTM D1922
Dart Drop Test 90.0 g
0.198 lb
ASTM D1709
Film Tensile Strength at Break, MD 26.9 MPa
3900 psi
ASTM D882
Film Tensile Strength at Break, TD 18.6 MPa
2700 psi
ASTM D882
1% Secant Modulus, MD 234 MPa
34000 psi
ASTM D882
1% Secant Modulus, TD 296 MPa
43000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 112 °C
233 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 7.3 %
7.3 %
ASTM D1003
Gloss 65 %
65 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Descriptive Properties Value Comments
Features Thermal Stabilizer