ExxonMobil LD 051.LT Shrink Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 051.LT Shrink Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 051 blown film resins are designed for demanding heavy duty film applications, and combine excellent strength properties with outstanding processability. Used in heavy duty shipping bags and shrink film.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ExxonMobil Method
Thickness 50.8 microns
2.00 mil
Melt Flow 0.25 g/10 min
0.25 g/10 min
ExxonMobil Method
Antiblock Level 3300 ppm
3300 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.7 MPa
1550 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 9.86 MPa
1430 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 130 %
130 %
ASTM D882
Film Elongation at Break, TD 590 %
590 %
ASTM D882
Film Elongation at Yield, MD 6.7 %
6.7 %
ASTM D882
Film Elongation at Yield, TD 5.0 %
5.0 %
ASTM D882
Elmendorf Tear Strength MD 330 g
330 g
ASTM D1922
Elmendorf Tear Strength TD 120 g
120 g
ASTM D1922
Elmendorf Tear Strength, MD 6.50 g/micron
165 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.36 g/micron
60.0 g/mil
ASTM D1922
Dart Drop 3.54 g/micron
90.0 g/mil
ASTM D1709
Dart Drop Test 180 g
0.397 lb
ASTM D1709
Film Tensile Strength at Break, MD 25.3 MPa
3670 psi
ASTM D882
Film Tensile Strength at Break, TD 24.3 MPa
3530 psi
ASTM D882
1% Secant Modulus, MD 186 MPa
27000 psi
ASTM D882
1% Secant Modulus, TD 245 MPa
35500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 109 °C
229 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 97.0 °C
207 °F
ExxonMobil Method
Vicat Softening Point 92.8 °C
199 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 20.5 %
20.5 %
ASTM D1003
Gloss 32 %
32 %
45°; ASTM D2457