ExxonMobil HD 6706.62 Injection Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil HD 6706.62 Injection Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: HD 6706 is a narrow molecular weight hexane copolymer designed for good processability and excellent balance of ESR, Toughness and Stiffness properties. This resin is ideally suited for heavy-duty applications that require robust performance in conditions ranging from ambient to sub-zero temperatures.Availability: Latin America, North America and South America Additive: Antioxidant: YesApplications: Industrial ComponentsIndustrial PailsLawn & Garden AccessoriesQuality HousewaresStructural Foam Articles Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D4883
Environmental Stress Crack Resistance 4.0 hour
4.0 hour
Cond. B, 10%; ASTM D1693
Melt Flow 6.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 26.2 MPa
3800 psi
ASTM D638
Elongation at Break 1300 %
1300 %
ASTM D638
Flexural Modulus 1.10 GPa
160 ksi
2% Secant; ASTM D790
Flexural Modulus, 1% Secant 1310 MPa
190000 psi
ASTM D790
Izod Impact, Notched 0.491 J/cm

@Temperature -40.0 °C
0.920 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 132 °C
270 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 66.7 °C
152 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 40.5 °C
105 °F
ASTM D648
Descriptive Properties Value Comments
Features Anti-static Agent
Form Pellet