ExxonMobil Escorene® LD 720.01 Specialty Film Resin

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer	Exxon Chemical
Trade Name	Escorene®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD 720.01 Specialty Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Escorene Ultra LD 720 resins are high vinyl acetate copolymer specialty film resins designed for applications requiring outstanding heat sealability, along with excellent strength properties and toughness. These resins are also used in specialized molding applications.Availability: Latin America, North America and South America Additive: Antiblock: 10000 ppmSlip: 7050 ppm Thermal Stabilizer: Yes Applications:Heat Seal LayerInjection MoldingShoe SolesInformation provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.941 g/cc	0.0340 lb/in³	ExxonMobil Method
Vinyl Acetate Content	18.5 %	18.5 %	ExxonMobil Method
Melt Flow	1.60 g/10 min @Load 2.16 kg, Temperature 190 °C	1.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ExxonMobil Method
Antiblock Level	10000 ppm	10000 ppm
Slip Level	7050 ppm	7050 ppm

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	180 %	180 %	ASTM D882
Film Elongation at Break, TD	650 %	650 %	ASTM D882
Elmendorf Tear Strength MD	40 g	40 g	ASTM D1922
Elmendorf Tear Strength TD	80 g	80 g	ASTM D1922
Dart Drop Test	370 g	0.816 lb	ASTM D1709A
Film Tensile Strength at Break, MD	26.9 MPa	3900 psi	ASTM D882
Film Tensile Strength at Break, TD	27.6 MPa	4000 psi	ASTM D882
1% Secant Modulus, MD	65.5 MPa	9500 psi	ASTM D882
1% Secant Modulus, TD	68.9 MPa	10000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	86.1 °C	187 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	62.2 °C	144 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	28 %	28 %	ASTM D1003
Gloss	49 %	49 %	45°C; ASTM D2457