ExxonMobil EXACT™ 3139 Plastomer for Cast Film Applications

Category	Polymer , Film , Thermoplastic , Elastomer, TPE
Manufacturer	Exxon Chemical
Trade Name	EXACT™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil EXACT™ 3139 Plastomer for Cast Film Applications.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Exact 3139 is an ethylene-based hexene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 3139 is designed for both monolayer and multilayer coextruded cast film applicatiosn requiring excellent toughness and heat seal performance. Typical applications include food packaging seal layers and lamination films. Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications:Cast FilmLamination Film Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ExxonMobil Method
Thickness	25.4 microns	1.00 mil
Melt Flow	7.5 g/10 min	7.5 g/10 min	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	5.24 MPa	760 psi	ASTM D882
Film Tensile Strength at Yield, TD	4.48 MPa	650 psi	ASTM D882
Film Elongation at Break, MD	530 %	530 %	ASTM D882
Film Elongation at Break, TD	700 %	700 %	ASTM D882
Film Elongation at Yield, MD	10.2 %	10.2 %	ASTM D882
Film Elongation at Yield, TD	8.1 %	8.1 %	ASTM D882
Puncture Energy	5.29 J	3.90 ft-lb	ExxonMobil Method
Elmendorf Tear Strength, MD	13.8 g/micron	350 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	25.2 g/micron	640 g/mil	ASTM D1922
Dart Drop	9.45 g/micron	240 g/mil	ASTM D1709A
Film Tensile Strength at Break, MD	65.8 MPa	9540 psi	ASTM D882
Film Tensile Strength at Break, TD	55.6 MPa	8060 psi	ASTM D882
1% Secant Modulus, MD	67.6 MPa	9800 psi	ASTM D882
1% Secant Modulus, TD	75.8 MPa	11000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	94.4 °C	202 °F	Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature	78.0 °C	172 °F	ExxonMobil Method
Vicat Softening Point	80.0 °C	176 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	0.50 %	0.50 %	ASTM D1003
Gloss	92 %	92 %	ASTM D2457

Descriptive Properties	Value	Comments
Puncture Force	11 lbf	ExxonMobil Method

Users viewing this material also viewed the following: