ExxonMobil Bicor® 50 LBW OPP Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor® 50 LBW OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Bicor LBW is a two-sided treated, slip modified, non-heat sealable OPP film designed for use as the outside web of a lamination. The print surface is treated and can be printed with water-based or solvent-based flexo and gravure inks and is the intended print and laminating surface.Availability: Latin America, North America and South AmericaKey Features:Excellent ink adhesion and bond strength in adhesive, PVdC adhesive, and extrusion laminationsApplications:BakeryBiscuits/Cookie/Crackers Confectionery, Gum Confectionery, SugarCrisps and SnacksFresh Produce Uses:HFFS Flexible Packaging VFFS Flexible PackagingProcessing Method: Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Water Vapor Transmission 10.9 g/m²/day
0.702 g/100 in²/day
38°C, 90% RH; ExxonMobil Method
Thickness 12.7 microns
0.500 mil
Nominal; ExxonMobil Method
Coating Weight 11.4 g/m²
7.10 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Coefficient of Friction 0.35
0.35
slip modified; ExxonMobil Method
Film Tensile Strength at Break, MD 131 MPa
19000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 234 MPa
34000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 6.0 %
6.0 %
at 275°F; ExxonMobil Method
Shrinkage, TD 6.0 %
6.0 %
at 275°F; ExxonMobil Method
Optical Properties Metric English Comments
Haze 1.7 %
1.7 %
ExxonMobil Method
Gloss 90 %
90 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Wetting Tension 0.8 receding COS theta
slip modified surface
0.85 receding COS theta
high energy surface
Yield 61200 in2/lb