ExxonMobil Bicor® 100 CSR-2 OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 100 CSR-2 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor CSR-2 is a one-side treated OPP film designed for cold seal release, either unsupported or as the outer web of a lamination.Availability: Latin America, North America and South AmericaKey Features:Excellent cold seal adhesion and ink adhesion on the treated surfaceNon-migratory slip system for consistent COFExcellent release from cold seal adhesivesApplications:BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateDairy ProductsFresh Produce Uses:HFFS Flexible Packaging VFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 5.10 g/m²/day | 0.328 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 25.4 microns | 1.00 mil | Nominal; ExxonMobil Method |
| Coating Weight | 22.7 g/m² | 14.2 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.20 | 0.20 | slip modified; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 145 MPa | 21000 psi | ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42000 psi | ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ExxonMobil Method |
| Gloss | 87 % | 87 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Wetting Tension | 0.83 receding COS theta | Treated Surface |
| Yield | 30400 in2/lb |
Users viewing this material also viewed the following:
- MV Labs MG200 MgBr2·6H2O Magnesium bromide hydrate
- SABIC Innovative Plastics Lexan® 121R PC (Asia Pacific)
- Huntsman Araldite GT 6450 Bisphenol A Epoxy Solid Resin
- Hyosung Topilene R200P PP
- LG Chemical Lupox® SG5152 PBT+PET+GF15%
- H.C. Starck Pure Molybdenum AB, Arc-Cast Bar
- Samsung Cheil Industries Starex® SP-0180 ABS, Unreinforced Extrusion Grade
- Shinkong Synthetic Fibers Shinite® PP4410 PP, Fire Retardant
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A
- BASF Elastollan® 1185A10U Wire & Cable Grade Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved