- Eurostar Starpylen MF007AS PP, Glass Fiber Filled, Injection Molded
Eurostar Starpylen MF007AS PP, Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen MF007AS PP, Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen MF007AS is a Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 50 mm/min; ISO 527 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 195 - 205 °C | 383 - 401 °F | |
| Zone 2 | 215 - 225 °C | 419 - 437 °F | |
| Zone 3 | 225 - 250 °C | 437 - 482 °F | |
| Melt Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible C8002 Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Geon™ Vinyl Flexible B6DB1 Polyvinyl Chloride, Flexible (PVC, Flexible)
- FKuR Kunststoff Terralene® WF 5525 Biobased Polyethylene
- Garlock 7797 Neoprene Sheet Rubber
- Schott N-SK11 Glass
- DSM Arnitel® PB420 TPC-ET
- Dow DS6D81 Polypropylene Random Copolymer Resin
- 3D Systems Accura® 50 Plastic for SLA® Systems
- 3M Scotchcal™ 1000-56 Graphic Film
Copyright © lookpolymers.com All Rights Reserved