- HOME
- POLYMER SEARCH
- Thermoplastic
- Polypropylene (PP)
- Polypropylene Glass Bead Filled
- Eurostar Starpylen MB006SU PP, Glass Bead Filled, Injection Molding Resin
Eurostar Starpylen MB006SU PP, Glass Bead Filled, Injection Molding Resin
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Glass Bead Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen MB006SU PP, Glass Bead Filled, Injection Molding Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen MB006SU is a Glass Bead Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm @Thickness 1.90 mm |
0.019 in/in @Thickness 0.0748 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.8 % | 4.8 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 42.0 MPa | 6090 psi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 104 µm/m-°C @Temperature 23.0 - 60.0 °C |
57.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 114 µm/m-°C @Temperature 23.0 - 60.0 °C |
63.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 195 - 205 °C | 383 - 401 °F | |
| Zone 2 | 215 - 225 °C | 419 - 437 °F | |
| Zone 3 | 225 - 250 °C | 437 - 482 °F | |
| Melt Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9945T TPE, ABS/PC Overmold
- Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK) (Unverified Data**)
- Lubriplate FML 1 Anhydrous Calcium USP Mineral Oil-Based Food Machinery Grade Grease
- Techmer ES HiFill® PA6/6 GF30 RM-1 L 30% Glass Filled
- Star Plastics PC1212FRRUV Molding Grade PC FR
- Styron EMERGEâ„¢ 4850-10 Polycarbonate
- Wellman Wellamid® GFX1717-N1 43% Glass Fiber Reinforced, Silicone Lubricated Nylon 66
- Dow VORANOL™ VORACTIV™ 6340 Catalytically Active Polyether Polyol
- ExxonMobil Escorene® HD-7755 HMW-HDPE Blown Film Resin (discontinued **)
- Reliance Industries LLDPE film - Active alumina + zeolite based film
Copyright © lookpolymers.com All Rights Reserved