EMS-Grivory Grivory® HT2V-45H PA6T/66-GF45

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® HT2V-45H PA6T/66-GF45.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grivory HT2V-45H is a 45% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation acc. to ISO: PA 6T/66 Acc. to ASTM: PPA, polyphthalamide. The main distinguishing feature of Grivory HT, when compared to other polyamides, is its good performance at high temperatures providing parts which are stiffer, stronger and have better heat distortion stability and chemical resistance. Grivory HT is suitable for production of technical parts in the application fields of: ElectroElectronicsAutomotiveSafety technologyMechanical engineeringInformation provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ISO 1183
Water Absorption 4.0 %
4.0 %
ISO 62
Moisture Absorption 1.40 %
1.40 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 310 MPa
45000 psi
dry; ISO 2039-1
310 MPa
45000 psi
conditioned; ISO 2039-1
Tensile Strength at Break 220 MPa
31900 psi
conditioned; ISO 527-1/-2
240 MPa
34800 psi
dry; ISO 527-1/-2
Elongation at Break 2.2 %
2.2 %
dry; ISO 527-1/-2
2.2 %
2.2 %
conditioned; ISO 527-1/-2
Tensile Modulus 15.5 GPa
2250 ksi
conditioned; ISO 527-1/-2
16.0 GPa
2320 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
dry; ISO 179/1eU
6.50 J/cm²
30.9 ft-lb/in²
conditioned; ISO 179/1eU
6.00 J/cm²

@Temperature 30.0 °C
28.6 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
6.00 J/cm²

@Temperature 30.0 °C
28.6 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
dry; ISO 179/1eA
1.10 J/cm²
5.23 ft-lb/in²
conditioned; ISO 179/1eA
0.900 J/cm²

@Temperature 30.0 °C
4.28 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
1.00 J/cm²

@Temperature 30.0 °C
4.76 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C
8.33 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C
33.3 µin/in-°F
ISO 11359-1/-2
Melting Point 310 °C
590 °F
10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air 140 °C
284 °F
long term; EMS
240 °C
464 °F
short term; EMS
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 235 °C
455 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
dry; IEC 60093
1.00e+12 ohm-cm
1.00e+12 ohm-cm
conditioned; IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Strength 38.0 kV/mm
965 kV/in
dry; IEC 60243-1
38.0 kV/mm
965 kV/in
conditioned; IEC 60243-1
Comparative Tracking Index 600 V
600 V
conditioned; IEC 60112
Descriptive Properties Value Comments
Automotive Exterior
Fuel systems
Interior
Powertrain and Chassis
Form Granules
Industry & Consumer goods Housewares
Hydraulics & Pneumatics
Mechanical Engineering
Power transmission
Sports & Leisure
Tools & Accessories
Processing Injection Molding
Special Characteristics Improved heat resistance
Improved UV resistance (outdoor use)
Copyright © lookpolymers.com All Rights Reserved