POLYMER SEARCH

EMS-Grivory Grivory® G 16 PA6I/6T

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® G 16 PA6I/6T.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grivory G 16 is a low viscosity amorphous copolyamide. It is suitable for injection - stretch blow molding, injection blow molding, extrusion blow molding, the manufacture of coextruded blown film and mono or coex cast film and extrusion of mono- and multilayer tubes. Grivory G 16 is also used as an additive for polyamide 6 and different copolyamides to improve film properties. Highly transparent and high surface glossVery good chemical resistanceVery good abrasion resistanceExcellent resistance to heat distortionExcellent flavor and aroma barrierLow transmission of UV-radiationImproved gas and aroma barrier at elevated relative humidity Barrier layer for mono- or co-extruded for packaging of cosmetics and foodstuffs. modifier of polyamide 6 barrier layers for flexible packaging of meat, cheese or any other foodstuff.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³	ISO 1183
Water Absorption	7.0 %	7.0 %	ISO 62
Moisture Absorption	2.00 %	2.00 %	ISO 62
Water Vapor Transmission	7.00 g/m²/day	0.451 g/100 in²/day	23°C/85%r.h.; DIS 15106-1/-2
Oxygen Transmission Rate	10.0 cc/m²/day	0.644 cc/100 in²/day	23°C/85%r.h.; DIS 15105-1/-2
	30.0 cc/m²/day	1.93 cc/100 in²/day	23°C/0%r.h.; DIS 15105-1/-2
Carbon Dioxide Transmission	40.0 cc-mm/m²-24hr-atm	102 cc-mil/100 in²-24hr-atm	23°C/85%r.h.; DIS 15105-1/-2
	90.0 cc-mm/m²-24hr-atm	229 cc-mil/100 in²-24hr-atm	23°C/0%r.h.; DIS 15105-1/-2
Melt Flow	100 g/10 min	100 g/10 min	(MVR) [cm³/10min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	85.0 MPa	12300 psi	ISO 527-3
Film Tensile Strength at Yield, TD	85.0 MPa	12300 psi	ISO 527-3
Film Elongation at Break, MD	200 %	200 %	ISO 527-3
Film Elongation at Break, TD	200 %	200 %	ISO 527-3
Film Elongation at Yield, MD	5.0 %	5.0 %	ISO 527-3
Film Elongation at Yield, TD	5.0 %	5.0 %	ISO 527-3
Tensile Modulus	3.00 GPa	435 ksi	conditioned; ISO 527-1/-2
	3.00 GPa	435 ksi	dry; ISO 527-1/-2
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	dry; ISO 179/1eA
	0.800 J/cm²	3.81 ft-lb/in²	conditioned; ISO 179/1eA
	0.200 J/cm² @Temperature 30.0 °C	0.952 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
	0.800 J/cm² @Temperature 30.0 °C	3.81 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
Tear Strength	5.00 kN/m	28.5 pli	Trouser Tear resistance MD; ISO 6383-1
	5.00 kN/m	28.5 pli	Trouser Tear resistance TD; ISO 6383-1
Elmendorf Tear Strength MD	1020 g	1020 g	ISO 6383-2
Elmendorf Tear Strength TD	1020 g	1020 g	ISO 6383-2
Film Tensile Strength at Break, MD	80.0 MPa	11600 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Transformation Temperature, Tg	125 °C	257 °F	10°C/min; ISO 11357-1/-2

Optical Properties	Metric	English	Comments
Gloss	160 %	160 %	60°; ISO 2813
Transmission, Visible	90 %	90 %	transparent; thickness not quantified

Descriptive Properties	Value	Comments
Food contact	EU Requirements
	FDA
Form	Granules
Packaging	Cosmetics / Personal care
	Paper coating
Processing	Injection Molding
Product Attributes	Barrier Properties
	Partially aromatic Polyamide
Special Characteristics	Transparent