E-Polymers SEPAZ® K115HF 15% Glass Fiber Reinforced High Flow PPS Resin
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | SEPAZ® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers SEPAZ® K115HF 15% Glass Fiber Reinforced High Flow PPS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyphenylene Sulfide Resin: High-performance engineering plastic SEPAZ PPS boasts excellent high-temperature resistance, flame retardancy and chemical resistance, physical strength, and its fluidity leads to good dimensional precision. SEPAZ PPS applications: switches, connectors and other electronic and electric components, alternators and other automobile components, and office equipment components including chassis parts and housings.Information Provided by E-Polymers Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
|
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 90.252 MPa | 13090 psi | ASTM D638 |
| Elongation at Break | 1.2 % | 1.2 % | ASTM D638 |
| Flexural Strength | 112.82 MPa | 16363 psi | ASTM D790 |
| Flexural Modulus | 7.9461 GPa | 1152.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.637 J/cm | 1.19 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 278 °C | 532 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 14.2 kV/mm @Thickness 1.60 mm |
361 kV/in @Thickness 0.0630 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 1.00e+6 Hz |
0.0010 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 300 - 330 °C | 572 - 626 °F | |
| Mold Temperature | 130 - 160 °C | 266 - 320 °F | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 6 hour | 6 hour |
Users viewing this material also viewed the following:
- LATI Latamid 6 H2 G/30-V0AF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Seals Eastern 7267 Ethylene-Propylene Rubber
- Struktol STRUKSILON 8017 Silicone Stabilizer for PU-Rigid Foam
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- Washington Penn Medium Impact Copolymer 10% Calcium Carbonate Filled
- Goodfellow Platinum 90/Rhodium 10 Thermocouple Alloy
- ELASTO UK Dryflex® 502900S SEBS Based Material, Unfilled Qualities, 90A Hardness, Black
- Buckeye Polymers BP ABS 4233 B ABS
- Osprey Metals 440C Stainless Steel Powder (Grade 90% - 22)
Copyright © lookpolymers.com All Rights Reserved