DuPont Performance Polymers Rynite® FG530 NC011 Polyethylene Terephthalate (PET) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer	DuPont Performance Polymers
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Rynite® FG530 NC011 Polyethylene Terephthalate (PET) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

30% Glass Reinforced Polyethylene Terephthalate Developed for Food Contact ApplicationsRynite FG530 NC011is a 30% glass fiber reinforced modified polyethylene terephthalate resin. It has been developed for consideration into applications for the food iInformation provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.57 g/cc	0.0567 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	162 MPa	23500 psi	ISO 527-1/-2
Elongation at Break	2.1 %	2.1 %	ISO 527-1/-2
Tensile Modulus	10.5 GPa	1520 ksi	ISO 527-1/-2
Charpy Impact Unnotched	4.00 J/cm²	19.0 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	1.10 J/cm²	5.23 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	257 °C	495 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	242 °C	468 °F	ISO 75-1/-2

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	250 V	250 V	IEC 60112

Descriptive Properties	Value	Comments
Additives	Release agent
Delivery Form	Pellets
Part Marking Code	>PET-GF30<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PET-GF30