DuPont Performance Polymers Zytel® HTN 54G15HSLR BK031 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 54G15HSLR BK031 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced Toughened PPA High Performance Polyamide Zytel HTN54G15HSLR BK031 is a 15% glass reinforced toughened heat stabilized hydrolysis resistant high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
DAM; ISO 1183
Viscosity Test 82 cm³/g
82 cm³/g
DAM; sulphuric acid 96%; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 118 MPa
17100 psi
50%RH; ISO 527-1/-2
125 MPa
18100 psi
DAM; ISO 527-1/-2
Tensile Stress 1.46 MPa

@Strain 0.0700 %,
Temperature 150 °C
212 psi

@Strain 0.0700 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
1.51 MPa

@Strain 0.0800 %,
Temperature 150 °C
219 psi

@Strain 0.0800 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
2.19 MPa

@Strain 0.0400 %,
Temperature 90.0 °C
318 psi

@Strain 0.0400 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
3.28 MPa

@Strain 0.0600 %,
Temperature 40.0 °C
476 psi

@Strain 0.0600 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
3.28 MPa

@Strain 0.130 %,
Temperature 90.0 °C
476 psi

@Strain 0.130 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
5.88 MPa

@Strain 0.105 %,
Temperature 40.0 °C
853 psi

@Strain 0.105 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
8.79 MPa

@Strain 0.580 %,
Temperature 150 °C
1270 psi

@Strain 0.580 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
10.99 MPa

@Strain 0.190 %,
Temperature 23.0 °C
1594 psi

@Strain 0.190 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
16.74 MPa

@Strain 1.04 %,
Temperature 150 °C
2428 psi

@Strain 1.04 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
19.78 MPa

@Strain 1.75 %,
Temperature 150 °C
2869 psi

@Strain 1.75 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
21.95 MPa

@Strain 1.14 %,
Temperature 90.0 °C
3184 psi

@Strain 1.14 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
25.79 MPa

@Strain 3.03 %,
Temperature 150 °C
3741 psi

@Strain 3.03 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
25.87 MPa

@Strain 0.450 %,
Temperature 0.000 °C
3752 psi

@Strain 0.450 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
26.28 MPa

@Strain 2.10 %,
Temperature 150 °C
3812 psi

@Strain 2.10 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
29.37 MPa

@Strain 0.490 %,
Temperature 0.000 °C
4260 psi

@Strain 0.490 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
32.1 MPa

@Strain 3.19 %,
Temperature 150 °C
4660 psi

@Strain 3.19 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
32.55 MPa

@Strain 10.45 %,
Temperature 150 °C
4721 psi

@Strain 10.45 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
33.94 MPa

@Strain 2.30 %,
Temperature 90.0 °C
4923 psi

@Strain 2.30 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
36.55 MPa

@Strain 0.580 %,
Temperature -20.0 °C
5301 psi

@Strain 0.580 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
37.17 MPa

@Strain 0.800 %,
Temperature 90.0 °C
5391 psi

@Strain 0.800 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
38.82 MPa

@Strain 8.44 %,
Temperature 150 °C
5630 psi

@Strain 8.44 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
39.76 MPa

@Strain 3.81 %,
Temperature 90.0 °C
5767 psi

@Strain 3.81 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
41.0 MPa

@Strain 0.730 %,
Temperature 23.0 °C
5950 psi

@Strain 0.730 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
44.03 MPa

@Strain 0.870 %,
Temperature 40.0 °C
6386 psi

@Strain 0.870 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
46.31 MPa

@Strain 0.780 %,
Temperature -20.0 °C
6717 psi

@Strain 0.780 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
51.76 MPa

@Strain 0.930 %,
Temperature 23.0 °C
7507 psi

@Strain 0.930 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
52.72 MPa

@Strain 1.21 %,
Temperature 90.0 °C
7646 psi

@Strain 1.21 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
61.97 MPa

@Strain 1.07 %,
Temperature 0.000 °C
8988 psi

@Strain 1.07 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
64.81 MPa

@Strain 1.42 %,
Temperature 40.0 °C
9400 psi

@Strain 1.42 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
65.83 MPa

@Strain 1.68 %,
Temperature 90.0 °C
9548 psi

@Strain 1.68 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
68.46 MPa

@Strain 1.23 %,
Temperature 0.000 °C
9929 psi

@Strain 1.23 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
70.74 MPa

@Strain 1.36 %,
Temperature 40.0 °C
10260 psi

@Strain 1.36 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
73.54 MPa

@Strain 1.41 %,
Temperature 23.0 °C
10670 psi

@Strain 1.41 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
76.12 MPa

@Strain 1.43 %,
Temperature 23.0 °C
11040 psi

@Strain 1.43 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
77.41 MPa

@Strain 1.91 %,
Temperature 40.0 °C
11230 psi

@Strain 1.91 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
82.59 MPa

@Strain 1.46 %,
Temperature -20.0 °C
11980 psi

@Strain 1.46 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
82.86 MPa

@Strain 1.44 %,
Temperature -20.0 °C
12020 psi

@Strain 1.44 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
86.51 MPa

@Strain 1.59 %,
Temperature 0.000 °C
12550 psi

@Strain 1.59 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
88.38 MPa

@Strain 1.84 %,
Temperature 23.0 °C
12820 psi

@Strain 1.84 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
91.4 MPa

@Strain 1.71 %,
Temperature 0.000 °C
13300 psi

@Strain 1.71 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
91.9 MPa

@Strain 1.91 %,
Temperature 40.0 °C
13300 psi

@Strain 1.91 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
98.87 MPa

@Strain 1.99 %,
Temperature 23.0 °C
14340 psi

@Strain 1.99 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
99.64 MPa

@Strain 1.82 %,
Temperature -20.0 °C
14450 psi

@Strain 1.82 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
101.68 MPa

@Strain 2.00 %,
Temperature 0.000 °C
14747 psi

@Strain 2.00 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
104.9 MPa

@Strain 1.95 %,
Temperature -20.0 °C
15210 psi

@Strain 1.95 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
105.67 MPa

@Strain 2.45 %,
Temperature 40.0 °C
15326 psi

@Strain 2.45 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
106.38 MPa

@Strain 2.08 %,
Temperature 0.000 °C
15429 psi

@Strain 2.08 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
113.82 MPa

@Strain 2.53 %,
Temperature 23.0 °C
16508 psi

@Strain 2.53 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
114.77 MPa

@Strain 2.18 %,
Temperature -20.0 °C
16646 psi

@Strain 2.18 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
120.69 MPa

@Strain 2.42 %,
Temperature -20.0 °C
17505 psi

@Strain 2.42 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
Elongation at Break 3.0 %
3.0 %
50%RH; ISO 527-1/-2
3.5 %
3.5 %
DAM; ISO 527-1/-2
Tensile Modulus 5.50 GPa
798 ksi
DAM; ISO 527-1/-2
6.10 GPa
885 ksi
50%RH; ISO 527-1/-2
Flexural Strength 210 MPa
30500 psi
DAM; ISO 178
Flexural Modulus 4.90 GPa
711 ksi
DAM; ISO 178
Secant Modulus 3.62 GPa

@Strain 2.32 %,
Temperature 40.0 °C
524 ksi

@Strain 2.32 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
3.84 GPa

@Strain 2.92 %,
Temperature 40.0 °C
557 ksi

@Strain 2.92 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
4.03 GPa

@Strain 3.02 %,
Temperature 23.0 °C
585 ksi

@Strain 3.02 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2