Ineos L06Z-00 Polypropylene Impact Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos L06Z-00 Polypropylene Impact Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a medium MFR impact copolymer polypropylene made for injection molded caps and closures applications. It offers a good balance of stiffness to impact resistance as compared to other impact copolymers of similar melt flow rate and comonomer content. It is formulated with nucleating agent, antistat and slip additives for fast mold setting and easy mold removal. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsCaps and closuresOther consumer product applicationsBenefitsGood drop impact resistanceGood stiffness to impact balanceFast crystallization rates for molding cycle reductionGood mold releaseInformation provided by Ineos Olefins & Polymers USA
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength, Yield | 30.3 MPa @Temperature 23.0 °C |
4400 psi @Temperature 73.4 °F |
ASTM D638 |
| Elongation at Yield | 6.3 % | 6.3 % | ASTM D638 |
| Flexural Modulus, 1% Secant | 1430 MPa @Temperature 23.0 °C |
207000 psi @Temperature 73.4 °F |
ASTM D790A |
| 1650 MPa @Temperature 23.0 °C |
240000 psi @Temperature 73.4 °F |
D790B | |
| Izod Impact, Notched | 0.854 J/cm @Temperature 0.000 °C |
1.60 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| 1.60 J/cm @Temperature 23.0 °C |
3.00 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Instrumented Impact (Dynatup) | Ductile break | 23°C, D3763 |
| Ductile break | 0°C, D3763 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ CPP GRC30 Copolymer Polypropylene Glass Reinforced
- Pau Tai UNISTAB BZ-434 Solid Complex Stabilizer
- Lanxess Pocan® BF 4232 000000 PBT, 30% Glass Fiber
- SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6
- Unifrax Anchor-Loc® 3000 Ceramic Fiber Modules
- Chase Plastics CP Pryme® PC300RHF Polycarbonate, Recycled Content
- A. Schulman POLYBATCH™ PT10327 Amber Concentrate Based in PET
- ExxonMobil Exceed™ 1518HA Metallocene Polyethylene Resin
- Denka REOMER G G5369 Thermoplastic Elastomer, For Extrusion
- Diamond Polymers ASA T-115
Copyright © lookpolymers.com All Rights Reserved