DuPont Performance Polymers Rynite® RE15022 NC010 PET (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Rynite® RE15022 NC010 PET
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rynite® RE15022 NC010 is a 36% glass reinforced product designed for applications that need high burst strength.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Filler Content | 36 % | 36 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 205 MPa @Temperature 23.0 °C |
29700 psi @Temperature 73.4 °F |
ISO 527 |
| Tensile Strength | 195 MPa @Temperature 23.0 °C |
28300 psi @Temperature 73.4 °F |
ASTM D638 |
| Elongation at Break | 2.4 % @Temperature 23.0 °C |
2.4 % @Temperature 73.4 °F |
ASTM D638 |
| 2.4 % @Temperature 23.0 °C |
2.4 % @Temperature 73.4 °F |
ISO 527 | |
| Tensile Modulus | 14.0 GPa @Temperature 23.0 °C |
2030 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 305 MPa @Temperature 23.0 °C |
44200 psi @Temperature 73.4 °F |
ASTM D790 |
| Flexural Modulus | 12.7 GPa @Temperature 23.0 °C |
1840 ksi @Temperature 73.4 °F |
ASTM D790 |
| Izod Impact, Notched | 1.05 J/cm @Temperature -40.0 °C |
1.97 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 1.10 J/cm @Temperature 23.0 °C |
2.06 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 11.75 J/cm @Temperature 23.0 °C |
22.01 ft-lb/in @Temperature 73.4 °F |
ASTM D4812 |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 247 °C | 477 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| 235 °C | 455 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | >= 95.0 °C | >= 203 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Drying Recommended | Yes | |
| Filler | Glass Reinforced | |
| Forms | Pellets | |
| Generic | PET | |
| Material Status | Preliminary Data | |
| Polymer Family | Polyester | |
| Polymer Type | PET | |
| Processing Method | Injection Molding | |
| Product Category | Glass/Mineral Reinforced Resins | |
| Region Available - Global | Yes | |
| RoHS Compliance | Contact Manufacturer |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ G-2175A PVC Compound
- Reade Advanced Materials Halloysite Clay (Al2Si2O5(OH)4)
- Karina 42/268-FC-LMP Red Color Concentrate for PVC
- Huntsman IROGRAN® A 92 P 4207 TPU-Polyether
- Loctite® 3321 Light Cure Acrylic Adhesive
- A. Schulman FORMION™ FI 342 Ionomer
- ExxonMobil PP7654KNE2 Polypropylene Homopolymer
- Eurostar Staramide AST03 PA66, Impact Modified, Injection Molded
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Suprex Clay Filler
Copyright © lookpolymers.com All Rights Reserved