- DuPont Performance Polymers Rynite® 940 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
DuPont Performance Polymers Rynite® 940 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass/Mineral Reinforced |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Rynite® 940 NC010 Polyethylene Terephthalate (PET)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glass/Mineral Reinforced Polyethylene TerephthalateInformation provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Water Absorption | 0.75 % @Thickness 2.00 mm |
0.75 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Moisture Absorption | 0.100 % @Thickness 2.00 mm |
0.100 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 2577 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
cm³/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0070 @Frequency 100 Hz |
0.0070 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Part Marking Code | >PET-(GF+MD)40< | ISO 11469 |
| Regional Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| Resin Identification | PET-(GF+MD)40 |
Users viewing this material also viewed the following:
- Pyrotek ISOFLOW Graphite Rings Graphite Rings for Billet Casting Molds
- Noltex Soarnol® DC3212 Ethylene Vinyl Alcohol Copolymer
- Ipiranga Petrochem LB 0117 LLDP
- Teknor Apex APEX® 3311-70 Polyvinyl Chloride, Flexible
- Tra-Con Tra-Coat WCC2B UV Curable Optical Adhesive
- Dow Corning XIAMETER® PMCPPMX-200 5,000CS Silicone Fluid
- Abatron AboCoat 8006-3/8606-3 Clear Versatile Epoxy
- Aclo Accutech Polypropylene Copolymer CP0437C40L1 Calcium Reinforced
- BASF Neopolen® P 8220 K 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- Anderman Ceramics EZC96P Zirconia, 96%, Calcia-Stabilized
Copyright © lookpolymers.com All Rights Reserved