DuPont Performance Polymers Rynite® 415HP NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® 415HP NC010 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced Polyethylene Terephthalate with Excellent Impact Resistance Rynite 415HP NC010 is a 15% glass reinforced modified polyethylene terephthalate improved for easy fast processing over a broad molding range with excellent balance of strInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 2.5 %

@Thickness 2.00 mm
 2.5 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.250 %

@Thickness 2.00 mm
 0.250 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 57000 cP

@Shear Rate 5000 1/s,
Temperature 315 °C
 57000 cP

@Shear Rate 5000 1/s,
Temperature 599 °F
 ISO 11403-1 -2
71000 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 71000 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
92000 cP

@Shear Rate 5000 1/s,
Temperature 275 °C
 92000 cP

@Shear Rate 5000 1/s,
Temperature 527 °F
 ISO 11403-1 -2
200000 cP

@Shear Rate 500 1/s,
Temperature 315 °C
 200000 cP

@Shear Rate 500 1/s,
Temperature 599 °F
 ISO 11403-1 -2
248000 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 248000 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
312000 cP

@Shear Rate 500 1/s,
Temperature 275 °C
 312000 cP

@Shear Rate 500 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
0.0050 cm/cm
0.0050 in/in
annealed; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
0.012 cm/cm
0.012 in/in
annealed; ISO 294-4
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 4.0 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 58
58
ISO 2039-2
Hardness, Rockwell R 111
111
ISO 2039-2
Tensile Strength at Break 79.0 MPa
11500 psi
ISO 527-1/-2
Tensile Stress 13.4 MPa

@Strain 1.00 %,
Temperature 150 °C
 1940 psi

@Strain 1.00 %,
Temperature 302 °F
 ISO 11403-1 -2
16.4 MPa

@Strain 0.450 %,
Temperature 40.0 °C
 2380 psi

@Strain 0.450 %,
Temperature 104 °F
 ISO 11403-1 -2
18.2 MPa

@Strain 0.350 %,
Temperature 23.0 °C
 2640 psi

@Strain 0.350 %,
Temperature 73.4 °F
 ISO 11403-1 -2
19.7 MPa

@Strain 0.300 %,
Temperature 0.000 °C
 2860 psi

@Strain 0.300 %,
Temperature 32.0 °F
 ISO 11403-1 -2
21.1 MPa

@Strain 1.00 %,
Temperature 90.0 °C
 3060 psi

@Strain 1.00 %,
Temperature 194 °F
 ISO 11403-1 -2
27.9 MPa

@Strain 0.350 %,
Temperature -20.0 °C
 4050 psi

@Strain 0.350 %,
Temperature -4.00 °F
 ISO 11403-1 -2
34.1 MPa

@Strain 4.00 %,
Temperature 150 °C
 4950 psi

@Strain 4.00 %,
Temperature 302 °F
 ISO 11403-1 -2
40.0 MPa

@Strain 7.00 %,
Temperature 150 °C
 5800 psi

@Strain 7.00 %,
Temperature 302 °F
 ISO 11403-1 -2
41.9 MPa

@Strain 10.0 %,
Temperature 150 °C
 6080 psi

@Strain 10.0 %,
Temperature 302 °F
 ISO 11403-1 -2
44.7 MPa

@Strain 4.00 %,
Temperature 90.0 °C
 6480 psi

@Strain 4.00 %,
Temperature 194 °F
 ISO 11403-1 -2
49.9 MPa

@Strain 7.00 %,
Temperature 90.0 °C
 7240 psi

@Strain 7.00 %,
Temperature 194 °F
 ISO 11403-1 -2
50.2 MPa

@Strain 1.80 %,
Temperature 40.0 °C
 7280 psi

@Strain 1.80 %,
Temperature 104 °F
 ISO 11403-1 -2
51.9 MPa

@Strain 10.0 %,
Temperature 90.0 °C
 7530 psi

@Strain 10.0 %,
Temperature 194 °F
 ISO 11403-1 -2
57.4 MPa

@Strain 1.40 %,
Temperature 23.0 °C
 8330 psi

@Strain 1.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
63.8 MPa

@Strain 1.20 %,
Temperature 0.000 °C
 9250 psi

@Strain 1.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2
67.5 MPa

@Strain 3.15 %,
Temperature 40.0 °C
 9790 psi

@Strain 3.15 %,
Temperature 104 °F
 ISO 11403-1 -2
71.3 MPa

@Strain 4.50 %,
Temperature 40.0 °C
 10300 psi

@Strain 4.50 %,
Temperature 104 °F
 ISO 11403-1 -2
77.6 MPa

@Strain 2.45 %,
Temperature 23.0 °C
 11300 psi

@Strain 2.45 %,
Temperature 73.4 °F
 ISO 11403-1 -2
84.5 MPa

@Strain 3.50 %,
Temperature 23.0 °C
 12300 psi

@Strain 3.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
86.3 MPa

@Strain 1.40 %,
Temperature -20.0 °C
 12500 psi

@Strain 1.40 %,
Temperature -4.00 °F
 ISO 11403-1 -2
91.6 MPa

@Strain 2.10 %,
Temperature 0.000 °C
 13300 psi

@Strain 2.10 %,
Temperature 32.0 °F
 ISO 11403-1 -2
109 MPa

@Strain 3.00 %,
Temperature 0.000 °C
 15800 psi

@Strain 3.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
116 MPa

@Strain 2.45 %,
Temperature -20.0 °C
 16800 psi

@Strain 2.45 %,
Temperature -4.00 °F
 ISO 11403-1 -2
128 MPa

@Strain 3.33 %,
Temperature -20.0 °C
 18600 psi

@Strain 3.33 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 5.0 %
5.0 %
ISO 527-1/-2
Tensile Modulus 4.70 GPa
682 ksi
ISO 527-1/-2
0.161 GPa

@Temperature 230 °C
 23.4 ksi

@Temperature 446 °F
 Dynamic; ISO 11403-1 -2
0.296 GPa

@Temperature 170 °C
 42.9 ksi

@Temperature 338 °F
 Dynamic; ISO 11403-1 -2
0.404 GPa

@Temperature 90.0 °C
 58.6 ksi

@Temperature 194 °F
 Dynamic; ISO 11403-1 -2
0.779 GPa

@Temperature 40.0 °C
 113 ksi

@Temperature 104 °F
 Dynamic; ISO 11403-1 -2
1.314 GPa

@Temperature -20.0 °C
 190.6 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.657 GPa

@Temperature -50.0 °C
 240.3 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Flexural Modulus 3.55 GPa
515 ksi
ISO 178
Shear Modulus 0.303 GPa

@Temperature 160 °C
 43.9 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.333 GPa

@Temperature 120 °C
 48.3 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.486 GPa

@Temperature 70.0 °C
 70.5 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.992 GPa

@Temperature 20.0 °C
 144 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.314 GPa

@Temperature -20.0 °C
 190.6 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.657 GPa

@Temperature -50.0 °C
 240.3 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Shear Strength 0.100 MPa

@Shear Rate 500 1/s,
Temperature 315 °C
 14.5 psi

@Shear Rate 500 1/s,
Temperature 599 °F
 ISO 11403-1 -2
0.124 MPa

@Shear Rate 500 1/s,
Temperature 295 °C
 18.0 psi

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
0.156 MPa

@Shear Rate 500 1/s,
Temperature 275 °C
 22.6 psi

@Shear Rate 500 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Secant Modulus 1.94 GPa

@Strain 3.60 %,
Temperature 40.0 °C
 282 ksi

@Strain 3.60 %,
Temperature 104 °F
 ISO 11403-1 -2
2.79 GPa

@Strain 1.80 %,
Temperature 40.0 °C
 405 ksi

@Strain 1.80 %,
Temperature 104 °F
 ISO 11403-1 -2
2.89 GPa

@Strain 2.80 %,
Temperature 23.0 °C
 420 ksi

@Strain 2.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.64 GPa

@Strain 0.450 %,
Temperature 40.0 °C
 529 ksi

@Strain 0.450 %,
Temperature 104 °F
 ISO 11403-1 -2
4.09 GPa

@Strain 2.40 %,
Temperature 0.000 °C
 593 ksi

@Strain 2.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
4.10 GPa

@Strain 1.40 %,
Temperature 23.0 °C
 595 ksi

@Strain 1.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2