DuPont Performance Polymers Hytrel® SC988 NC010 TPC-ET (Unverified Data**)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Hytrel® SC988 NC010 TPC-ET (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Hytrel® SC988 NC010 is the highest modulus grade, with nominal hardness of 82D, contains a non-discoloring stabilizer. Can be processed by various thermoplastic processing techniques. Developed for applications such as parts for the healthcare industry.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	<= 82	<= 82	ISO 868
Tensile Strength at Break	50.0 MPa @Temperature 23.0 °C	7250 psi @Temperature 73.4 °F	ISO 527 (1BA bar)
Elongation at Break	400 % @Temperature 23.0 °C	400 % @Temperature 73.4 °F	ISO 527 (1BA bar)
Tensile Modulus	1.18 GPa @Temperature 23.0 °C	171 ksi @Temperature 73.4 °F	ISO 527
Charpy Impact, Notched	1.50 J/cm² @Temperature 23.0 °C	7.14 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	221 °C	430 °F	10°C/min; ISO 11357-1/-3

Descriptive Properties	Value	Comments
Additive	Antioxidant
Appearance	Natural Color
	Natural Color
Features	Chemical Resistance
	Creep Resistance, Good
	Energy Absorption, High
	Food Contact Acceptable
	Hardness, High
	Noise Dampening
Forms	Pellets
Generic	TPC-ET
Material Status	Preliminary Data
Part Marking Code	>TPC-ET<	ISO 11469
Processing Method	Casting
	Extrusion Resins
	Injection Molding
Product Category	Extrusion Resins
	Healthcare Resins
Region Available - Global	Yes
Resin Identification	TPC-ET	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Medical Applications