DuPont Performance Polymers Hytrel® RS 40F5 NC010 Polyester Elastomer TPC-ET (Unverified Data**)

Category	Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer	DuPont Performance Polymers
Trade Name	Hytrel® RS
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Hytrel® RS 40F5 NC010 Polyester Elastomer TPC-ET (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

40 Shore D Renewably Sourced Medium Viscosity Polyester Elastomer Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.11 g/cc	0.0401 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0090 cm/cm	0.0090 in/in	ISO 294-4 2577
	0.010 cm/cm	0.010 in/in	48h at 80°C; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ISO 294-4 2577
	0.0080 cm/cm	0.0080 in/in	48h at 80°C; ISO 294-4
Melt Flow	9.0 g/10 min @Load 2.16 kg, Temperature 220 °C	9.0 g/10 min @Load 4.76 lb, Temperature 428 °F	cm³/10min; ISO 1133
	9.0 g/10 min @Load 2.16 kg, Temperature 220 °C	9.0 g/10 min @Load 4.76 lb, Temperature 428 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	33	33	15s; ISO 868
	<= 37	<= 37	ISO 868
Tensile Strength at Break	25.0 MPa	3630 psi	ISO 527-1/-2
Tensile Stress	2.10 MPa @Strain 5.00 %	305 psi @Strain 5.00 %	ISO 527-1/-2
	3.50 MPa @Strain 10.0 %	508 psi @Strain 10.0 %	ISO 527-1/-2
	6.70 MPa @Strain 50.0 %	972 psi @Strain 50.0 %	ISO 527-1/-2
Elongation at Break	>= 300 %	>= 300 %	ISO 527-1/-2
	800 %	800 %	Nominal; ISO 527-1/-2
Tensile Modulus	0.0450 GPa	6.53 ksi	ISO 527-1/-2
Flexural Modulus	0.0500 GPa	7.25 ksi	ISO 178
Shear Strength	0.1335 MPa @Shear Rate 500 1/s, Temperature 230 °C	19.36 psi @Shear Rate 500 1/s, Temperature 446 °F	ISO 11403-1 -2
	0.176 MPa @Shear Rate 500 1/s, Temperature 210 °C	25.5 psi @Shear Rate 500 1/s, Temperature 410 °F	ISO 11403-1 -2
	0.2305 MPa @Shear Rate 500 1/s, Temperature 190 °C	33.43 psi @Shear Rate 500 1/s, Temperature 374 °F	ISO 11403-1 -2
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	NB	NB	ISO 179/1eA
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eA
	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ISO 179/1eA
Tear Strength	101 kN/m	576 pli	parallel; ISO 34-1
	103 kN/m	588 pli	normal; ISO 34-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	210 µm/m-°C	117 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	200 µm/m-°C	111 µin/in-°F	ISO 11359-1/-2
Melting Point	190 °C	374 °F	10°C/min; ISO 11357-1/-3
Brittleness Temperature	-95.0 °C	-139 °F	ISO 974
	-95.0 °C	-139 °F	ISO 6603-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
Oxygen Index	20 %	20 %	ISO 4589-1/-2