DuPont Performance Polymers Hytrel® 5553FG NC010 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 5553FG NC010 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
55 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
DS
1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.60 %

@Thickness 2.00 mm
 0.60 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 cm³/10min; ISO 1133
8.0 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 8.0 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 51
51
15s; ISO 868
<= 56
<= 56
ISO 868
Tensile Strength at Break 40.0 MPa
5800 psi
ISO 527-1/-2
Tensile Stress 6.60 MPa

@Strain 5.00 %
 957 psi

@Strain 5.00 %
 ISO 527-1/-2
10.2 MPa

@Strain 10.0 %
 1480 psi

@Strain 10.0 %
 ISO 527-1/-2
15.0 MPa

@Strain 100 %
 2180 psi

@Strain 100 %
 ISO 527-1/-2
3.97 MPa

@Strain 6.94 %,
Temperature 120 °C
 576 psi

@Strain 6.94 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.65 MPa

@Strain 6.90 %,
Temperature 100 °C
 674 psi

@Strain 6.90 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.93 MPa

@Strain 6.00 %,
Temperature 90.0 °C
 715 psi

@Strain 6.00 %,
Temperature 194 °F
 ISO 11403-1 -2
4.97 MPa

@Strain 6.87 %,
Temperature 90.0 °C
 721 psi

@Strain 6.87 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
5.78 MPa

@Strain 16.44 %,
Temperature 120 °C
 838 psi

@Strain 16.44 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.37 MPa

@Strain 26.67 %,
Temperature 120 °C
 924 psi

@Strain 26.67 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.55 MPa

@Strain 36.16 %,
Temperature 120 °C
 950 psi

@Strain 36.16 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.62 MPa

@Strain 46.39 %,
Temperature 120 °C
 960 psi

@Strain 46.39 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.70 MPa

@Strain 58.81 %,
Temperature 120 °C
 972 psi

@Strain 58.81 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.83 MPa

@Strain 71.96 %,
Temperature 120 °C
 991 psi

@Strain 71.96 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.84 MPa

@Strain 7.55 %,
Temperature 60.0 °C
 992 psi

@Strain 7.55 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
6.97 MPa

@Strain 85.11 %,
Temperature 120 °C
 1010 psi

@Strain 85.11 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.98 MPa

@Strain 17.06 %,
Temperature 100 °C
 1010 psi

@Strain 17.06 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.12 MPa

@Strain 98.26 %,
Temperature 120 °C
 1030 psi

@Strain 98.26 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.41 MPa

@Strain 117.99 %,
Temperature 120 °C
 1070 psi

@Strain 117.99 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.46 MPa

@Strain 6.00 %,
Temperature 40.0 °C
 1080 psi

@Strain 6.00 %,
Temperature 104 °F
 ISO 11403-1 -2
7.51 MPa

@Strain 16.99 %,
Temperature 90.0 °C
 1090 psi

@Strain 16.99 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.67 MPa

@Strain 27.23 %,
Temperature 100 °C
 1110 psi

@Strain 27.23 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.67 MPa

@Strain 131.14 %,
Temperature 120 °C
 1110 psi

@Strain 131.14 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.88 MPa

@Strain 37.39 %,
Temperature 100 °C
 1140 psi

@Strain 37.39 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.90 MPa

@Strain 6.00 %,
Temperature 23.0 °C
 1150 psi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.96 MPa

@Strain 46.83 %,
Temperature 100 °C
 1150 psi

@Strain 46.83 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.04 MPa

@Strain 60.62 %,
Temperature 100 °C
 1170 psi

@Strain 60.62 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.07 MPa

@Strain 147.21 %,
Temperature 120 °C
 1170 psi

@Strain 147.21 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.17 MPa

@Strain 73.69 %,
Temperature 100 °C
 1180 psi

@Strain 73.69 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.30 MPa

@Strain 27.11 %,
Temperature 90.0 °C
 1200 psi

@Strain 27.11 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.32 MPa

@Strain 86.76 %,
Temperature 100 °C
 1210 psi

@Strain 86.76 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.52 MPa

@Strain 100.56 %,
Temperature 100 °C
 1240 psi

@Strain 100.56 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.52 MPa

@Strain 24.0 %,
Temperature 90.0 °C
 1240 psi

@Strain 24.0 %,
Temperature 194 °F
 ISO 11403-1 -2
8.56 MPa

@Strain 37.24 %,
Temperature 90.0 °C
 1240 psi

@Strain 37.24 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.65 MPa

@Strain 47.36 %,
Temperature 90.0 °C
 1250 psi

@Strain 47.36 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.67 MPa

@Strain 7.52 %,
Temperature 40.0 °C
 1260 psi

@Strain 7.52 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
8.76 MPa

@Strain 170.59 %,
Temperature 120 °C
 1270 psi

@Strain 170.59 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.78 MPa

@Strain 60.37 %,
Temperature 90.0 °C
 1270 psi

@Strain 60.37 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.85 MPa

@Strain 120.16 %,
Temperature 100 °C
 1280 psi

@Strain 120.16 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.94 MPa

@Strain 73.39 %,
Temperature 90.0 °C
 1300 psi

@Strain 73.39 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.14 MPa

@Strain 87.12 %,
Temperature 90.0 °C
 1330 psi

@Strain 87.12 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.17 MPa

@Strain 133.96 %,
Temperature 100 °C
 1330 psi

@Strain 133.96 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.33 MPa

@Strain 100.14 %,
Temperature 90.0 °C
 1350 psi

@Strain 100.14 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.60 MPa

@Strain 196.16 %,
Temperature 120 °C
 1390 psi

@Strain 196.16 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.61 MPa

@Strain 150.65 %,
Temperature 100 °C
 1390 psi

@Strain 150.65 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.71 MPa

@Strain 120.38 %,
Temperature 90.0 °C
 1410 psi

@Strain 120.38 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.82 MPa

@Strain 17.63 %,
Temperature 60.0 °C
 1420 psi

@Strain 17.63 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
10.01 MPa

@Strain 133.4 %,
Temperature 90.0 °C
 1452 psi

@Strain 133.4 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.32 MPa

@Strain 173.89 %,
Temperature 100 °C
 1497 psi

@Strain 173.89 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.4 MPa

@Strain 6.00 %,
Temperature 0.000 °C
 1510 psi

@Strain 6.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.45 MPa

@Strain 150.03 %,
Temperature 90.0 °C
 1516 psi

@Strain 150.03 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.71 MPa

@Strain 28.42 %,
Temperature 60.0 °C
 1553 psi

@Strain 28.42 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
10.92 MPa

@Strain 38.49 %,
Temperature 60.0 °C
 1584 psi

@Strain 38.49 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
10.98 MPa

@Strain 48.56 %,
Temperature 60.0 °C
 1593 psi

@Strain 48.56 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
11.12 MPa

@Strain 62.95 %,
Temperature 60.0 °C
 1613 psi

@Strain 62.95 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2