DuPont Performance Polymers GLT305 Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinued **)
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers GLT305 Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationViton® GLT305
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 34 @Temperature 121 °C |
34 @Temperature 250 °F |
ML-10 (gum)-Akron data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 18.2 MPa | 2640 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 186 % | 186 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00670 GPa | 0.972 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 29 % @Temperature 200 °C |
29 % @Temperature 392 °F |
Method B, O-rings 70 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -30.8 °C | -23.4 °F | DSC, modulated |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PS-20GF/000 NATURAL Polybutylene Terephthalate (PBT)
- Polymax® Maxelast® D6780 TPE, Extruded
- Lucent Polymers GPP-230 Polypropylene, 30% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
- Lucent Polymers TPP-230 Polypropylene, 30% Talc Filled, Impact Modified
- Shandong Dongyue Shenzhou New Material Co Hexafluoropropene Oxide (HFPO)
- SABIC Innovative Plastics Valox® EH7020 PBT (Asia Pacific)
- The NanoSteel® Company SHS 9172 HVOF Steel Alloy, Atomized Powder
- DuPont Elvaloy® 3117 AC Ethylene and 17% Butyl Acrylate Copolymer
- Lubrizol ESTANE® 58447 Ester Based Thermoplastic Polyurethane (European Grade)
- SABIC Innovative Plastics PC2200 PC
Copyright © lookpolymers.com All Rights Reserved