SABIC Innovative Plastics ULTEM HU2100 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM HU2100 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocompatible (ISO 10993 or USP Class VI). RoHS compliant. UL94 V0 and 5VA listed.
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Moisture Absorption 0.600 %
0.600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.0 %
1.0 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 5.0 g/10 min

@Load 3.80 kg,
Temperature 200 °C
 5.0 g/10 min

@Load 8.38 lb,
Temperature 392 °F
 ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 9.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
115 MPa
16700 psi
5 mm/min; ISO 527
Tensile Strength, Yield 114 MPa
16500 psi
Type I, 5 mm/min; ASTM D638
115 MPa
16700 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
5 mm/min; ISO 527
6.0 %
6.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
5 mm/min; ISO 527
6.0 %
6.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.50 GPa
653 ksi
1 mm/min; ISO 527
4.68 GPa
679 ksi
5 mm/min; ASTM D638
Flexural Strength 185 MPa
26800 psi
2 mm/min; ISO 178
Flexural Yield Strength 160 MPa
23200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 4.50 GPa
653 ksi
2 mm/min; ISO 178
5.50 GPa
798 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
0.530 J/cm

@Temperature -30.0 °C
 0.993 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
 7.38 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 26.0 µm/m-°C

@Temperature 23.0 - 150 °C
 14.4 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
32.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 18.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
60.0 µm/m-°C

@Temperature 23.0 - 150 °C
 33.3 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
205 °C

@Thickness 3.20 mm
 401 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 212 °C
414 °F
Rate B/50; ISO 306
217 °C
423 °F
Rate B/120; ISO 306
223 °C
433 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Electrical Properties Metric English Comments
Dielectric Strength 15.0 kV/mm

@Thickness 3.20 mm
 381 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Comparative Tracking Index 150 V
150 V
IEC 60112