DuPont Performance Polymers Delrin® 588P NC010 Acetal (POM)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Delrin® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Delrin® 588P NC010 Acetal (POM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nucleated Medium Viscosity Acetal HomopolymerInformation provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % @Thickness 2.00 mm |
0.30 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 2577 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C |
15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527-1/-2 |
| Elongation at Break | 25 % | 25 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 12 % | 12 % | ISO 527-1/-2 |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527-1/-2 |
| Flexural Modulus | 3.05 GPa | 442 ksi | ISO 178 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Delivery Form | Pellets | |
| Part Marking Code | POM | ISO 11469 |
| Regional Availability | Asia Pacific | |
| Resin Identification | POM | ISO 1043 |
| UL recognition | UL |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers KetaSpire® KT-850P Polyetheretherketone (PEEK) (Unverified Data**)
- Overview of materials for Nylon 6, 30% Mineral Filled
- Global PC-1415-R General Purpose Polycarbonate
- SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer
- Solvay Specialty Polymers Polymist® XPP 541 Polytetrafluoroethylene (PTFE)
- Spartech Plasticor Fluted PP Co/Pol Corrugated Sheet
- Shuman 780 Grey ABS
- ExxonMobil Exxsol™ D110 Dearomatized Fluid
- Arlon 56811B025 0.026" (0.660 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M HQ-115IL Ionic Liquid Precursor
Copyright © lookpolymers.com All Rights Reserved