DuPont Performance Polymers Delrin® 100TE NC010 Acetal (POM) (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced, Impact Grade
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 100TE NC010 Acetal (POM) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Toughened High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 100TE NC010 (formerly DE20580) is a high viscosity toughened acetal homopolymer with very low VOC emissions. Processing methods include injection molding.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.016 cm/cm	0.016 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.017 cm/cm	0.017 in/in	ISO 294-4 2577
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	cm³/10min; ISO 1133
	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	54.0 MPa	7830 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	Nominal; ISO 527-1/-2
Elongation at Yield	25 %	25 %	ISO 527-1/-2
Tensile Modulus	1.85 GPa	268 ksi	ISO 527-1/-2
Flexural Strength	51.0 MPa @Strain 3.50 %	7400 psi @Strain 3.50 %	ISO 178
Flexural Modulus	1.85 GPa	268 ksi	ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
Charpy Impact, Notched	2.50 J/cm²	11.9 ft-lb/in²	ISO 179/1eA
	1.40 J/cm² @Temperature -30.0 °C	6.66 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	120 µm/m-°C	66.7 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	120 µm/m-°C	66.7 µin/in-°F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	126 °C	259 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	71.0 °C	160 °F	ISO 75-1/-2

Descriptive Properties	Value	Comments
Additives	Lubricants
	Release agent
Delivery Form	Pellets
Emissions	<2 mg/kg	VDA 275
Part Marking Code	>POM-I<	ISO 11469
Processing	Blow Moulding
	Coatable
	Injection Moulding
	Other Extrusion
	Profile Extrusion
	Sheet Extrusion
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	POM-I	ISO 1043