- DuPont Elvax® 40L-03 High Temperature Ignition Cable Jacket Formulation (discontinued **)
DuPont Elvax® 40L-03 High Temperature Ignition Cable Jacket Formulation (discontinued **)
| Category | Polymer , Thermoplastic , Ethylene Vinyl Acetate |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvax® 40L-03 High Temperature Ignition Cable Jacket Formulation
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvax® 40L-03 high temperature ignition cable jacket.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 17 @Temperature 100 °C |
17 @Temperature 212 °F |
ML 1 + 4; ASTM D1646 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength at Break | 9.40 MPa | 1360 psi | ASTM D412 |
| 9.40 MPa | 1360 psi | After 7 days/150°C air oven, ASTM D573 | |
| 9.96 MPa | 1440 psi | After 72hr/177°C air oven, ASTM D573 | |
| 6.58 MPa @Treatment Temp. 121 °C, Time 64800 sec |
954 psi @Treatment Temp. 250 °F, Time 18.0 hour |
in ASTM #2 Oil | |
| Elongation at Break | 331.2 % | 331.2 % | After 72hr/177°C air oven; ASTM D573 |
| 342 % | 342 % | After 7 days/150°C air oven; ASTM D573 | |
| 360 % | 360 % | ASTM D412 | |
| 216 % @Treatment Temp. 121 °C, Time 64800 sec |
216 % @Treatment Temp. 250 °F, Time 18.0 hour |
in ASTM #2 Oil | |
| Tear Strength | 6.20 kN/m | 35.4 pli | ASTM D470 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 14.5 kV/mm | 368 kV/in | ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| a,a'-bis [t-butylperoxy] diisopropylbenzene | 2.5 phr | |
| DLTDP | 1 phr | |
| Elvax® 40L-03 | 100 phr | |
| HVA-2 | 1 phr | |
| Hydrated Alumina | 75-90 phr | |
| Irganox 1010 | 2 phr | |
| Silquest A-172 | 1 phr | |
| SRF Carbon Black | 0-3 phr | |
| Stearic Acid | 1 phr |
Users viewing this material also viewed the following:
- Fainplast Compounds RI 54 Rigid PVC, Injection Molding
- Lehmann & Voss LUVOCOM® 1105-7583 PEEK, with glass fiber and PTFE, improved wear resistance
- SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12
- Dow Saran® 560 Vapor Retarder Film
- Fainplast Compounds HAX HF 039/31 Halogen Free PVC
- Carpenter Micro-Melt® M-4 Alloy (AISI M4)
- 3M Scotch-Weld™ DP640 Structural Adhesive
- Resinoid 7051 SS Phenolic Molding, Glass Reinforced
- Henkel SynCore HC 9875 Syntactic Film
- DuPont Performance Polymers Rynite® FG530 NC011 PET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved