Material Notes:
3M Fastbond™ Contact Adhesive 30-NF and 30H-NF are water-dispersed, sprayable contact adhesives for high immediate bond strength n long bonding range.Information provided by 3M
Physical Properties Metric English Comments
Solids Content 47 - 51 %
47 - 51 %
Brookfield Viscosity 200 - 750 cP
200 - 750 cP
RVF #2 sp @ 20 rpm @ 80°F
Mechanical Properties Metric English Comments
Tensile Strength at Break 0.186 MPa

@Temperature 93.0 °C
 27.0 psi

@Temperature 199 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
0.207 MPa

@Temperature 82.0 °C
 30.0 psi

@Temperature 180 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
0.379 MPa

@Temperature 66.0 °C
 55.0 psi

@Temperature 151 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
0.779 MPa

@Temperature 24.0 °C
 113 psi

@Temperature 75.2 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
Shear Strength 0.207 MPa

@Temperature 93.0 °C
 30.0 psi

@Temperature 199 °F
 Overlap, 1/8" birch 1/8" birch
0.207 MPa

@Temperature 82.0 °C
 30.0 psi

@Temperature 180 °F
 1/8" Birch/High-Pressure Laminate, no aging
0.276 MPa

@Temperature 102 °C
 40.0 psi

@Temperature 216 °F
 Overlap, 1/8" birch 1/8" birch
0.345 MPa

@Temperature 82.0 °C
 50.0 psi

@Temperature 180 °F
 1/8" Birch/High-Pressure Laminate, aged 9 mo
0.414 MPa

@Temperature 82.0 °C
 60.0 psi

@Temperature 180 °F
 Overlap, 1/8" birch 1/8" birch
0.517 MPa

@Temperature 82.0 °C
 75.0 psi

@Temperature 180 °F
 1/8" Birch/High-Pressure Laminate, aged 6 mo
0.552 MPa

@Temperature 82.0 °C
 80.0 psi

@Temperature 180 °F
 1/8" Birch/High-Pressure Laminate, aged 3 mo
0.862 MPa

@Temperature 66.0 °C
 125 psi

@Temperature 151 °F
 1/8" Birch/High-Pressure Laminate, aged 9 mo
0.896 MPa

@Temperature 66.0 °C
 130 psi

@Temperature 151 °F
 1/8" Birch/High-Pressure Laminate, no aging
0.965 MPa

@Temperature 66.0 °C
 140 psi

@Temperature 151 °F
 1/8" Birch/High-Pressure Laminate, aged 3 mo
1.03 MPa

@Temperature 66.0 °C
 150 psi

@Temperature 151 °F
 1/8" Birch/High-Pressure Laminate, aged 6 mo
1.83 MPa

@Temperature 24.0 °C
 265 psi

@Temperature 75.2 °F
 1/8" Birch/High-Pressure Laminate, no aging
1.97 MPa

@Temperature 24.0 °C
 285 psi

@Temperature 75.2 °F
 1/8" Birch/High-Pressure Laminate, aged 9 mo
2.10 MPa

@Temperature 24.0 °C
 305 psi

@Temperature 75.2 °F
 1/8" Birch/High-Pressure Laminate, aged 6 mo
2.17 MPa

@Temperature 24.0 °C
 315 psi

@Temperature 75.2 °F
 1/8" Birch/High-Pressure Laminate, aged 3 mo
3.31 MPa

@Temperature 24.0 °C
 480 psi

@Temperature 75.2 °F
 Overlap, 1/8" birch 1/8" birch
7.58 MPa

@Temperature -37.0 °C
 1100 psi

@Temperature -34.6 °F
 Overlap, 1/8" birch 1/8" birch
Peel Strength 0.877 kN/m

@Temperature -37.0 °C,
Time 1.81e+6 sec
 5.00 pli

@Temperature -34.6 °F,
Time 504 hour
 canvas/canvas
1.75 kN/m

@Temperature 66.0 °C,
Time 1.81e+6 sec
 10.0 pli

@Temperature 151 °F,
Time 504 hour
 canvas/canvas
1.75 kN/m

@Temperature 82.0 °C,
Time 1.81e+6 sec
 10.0 pli

@Temperature 180 °F,
Time 504 hour
 canvas/canvas
2.63 kN/m

@Temperature 24.0 °C,
Time 1.81e+6 sec
 15.0 pli

@Temperature 75.2 °F,
Time 504 hour
 canvas/canvas
3.51 kN/m

@Temperature 24.0 °C,
Time 605000 sec
 20.0 pli

@Temperature 75.2 °F,
Time 168 hour
 canvas/canvas
3.51 kN/m

@Temperature 24.0 °C,
Time 1.21e+6 sec
 20.0 pli

@Temperature 75.2 °F,
Time 336 hour
 canvas/canvas
4.38 kN/m

@Temperature 24.0 °C,
Time 86400 sec
 25.0 pli

@Temperature 75.2 °F,
Time 24.0 hour
 canvas/canvas
5.26 kN/m

@Temperature 24.0 °C,
Time 432000 sec
 30.0 pli

@Temperature 75.2 °F,
Time 120 hour
 canvas/canvas
6.14 kN/m

@Temperature 24.0 °C,
Time 259000 sec
 35.0 pli

@Temperature 75.2 °F,
Time 72.0 hour
 canvas/canvas
Descriptive Properties Value Comments
Appearance Green, Blue (Wet), Green (Dry); Neutral, White (Wet), Clear (Dry)
Base Polychloroprene