- Dow INSPIRE™ D7000 Thermoplastic Polyolefin (discontinued **)
Dow INSPIRE™ D7000 Thermoplastic Polyolefin (discontinued **)
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow INSPIRE™ D7000 Thermoplastic Polyolefin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010, although this grade had previously been removed from Dow's standard product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Filler Content | 24 % | 24 % | ISO 3451 |
| Melt Flow | 28 g/10 min @Load 2.16 kg, Temperature 230 °C |
28 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | ISO 868 |
| Tensile Strength, Yield | 22.2 MPa | 3220 psi | ISO R527 |
| Flexural Modulus | 2.1060 GPa | 305.45 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | NB; ISO 180/1A |
| 2.00 kJ/m² @Temperature -40.0 °C |
0.952 ft-lb/in² @Temperature -40.0 °F |
ISO 180/1A | |
| 15.0 kJ/m² @Temperature 10.0 °C |
7.14 ft-lb/in² @Temperature 50.0 °F |
ISO 180/1A | |
| Falling Dart Impact | 34.0 J | 25.1 ft-lb | @ 23°C, 6.7 m/s; ASTM D3763 |
| 36.1 J | 26.6 ft-lb | @ 0°C, 6.7 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 59.0 µm/m-°C @Temperature 20.0 °C |
32.8 µin/in-°F @Temperature 68.0 °F |
ASTM D228 |
| Deflection Temperature at 0.46 MPa (66 psi) | 117.0 °C | 242.6 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.00 °C | 141.8 °F | ISO 75 |
| Flame Spread | 39.0 mm/min | 1.54 in/min |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Five Finger Scratch (N) | 15 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 180 (2400 Viscosity) Rapid Bonding Adhesive
- LG Chemical LI911 ASA
- ICE Al2O3 96
- SABIC Innovative Plastics LNP THERMOCOMP BFL2200 PC (Asia Pacific)
- SABIC Innovative Plastics Noryl EBN3001 PPE+HIPS (Asia Pacific)
- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness,
- A. Schulman POLYBATCH™ Red LL50304/3 Concentrate Based In LLDPE
- ThyssenKrupp COR-TEN B Structural Steel
- 3M FV010002 Removable Vinyl Label Product
Copyright © lookpolymers.com All Rights Reserved