Bulk Molding Compounds BMC 1410 Electrical Grade

Category Polymer , Thermoset , Polyester, TS
Manufacturer BMC - Bulk Molding Compounds Inc.
Trade Name BMC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bulk Molding Compounds BMC 1410 Electrical Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMC 1410 is a high-strength electrical grade material with excellent flammability resistance. In most applications, this material is competitive with SMC. Equal performance at a lower cost. Normally compression molded, but has been successfully injection molded in a number of applications. UL® recognized. This material was formerly known as Glastic® 1410.
Physical Properties Metric English Comments
Specific Gravity 1.83 - 1.89 g/cc
1.83 - 1.89 g/cc
Water Absorption 0.18 - 0.24 %
0.18 - 0.24 %
24 hours, 23°C
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Mechanical Properties Metric English Comments
Hardness, Barcol 40 - 50
40 - 50
Tensile Strength, Ultimate 27.6 - 34.5 MPa
4000 - 5000 psi
Flexural Strength 179 - 193 MPa
26000 - 28000 psi
Flexural Modulus 15.2 - 16.5 GPa
2200 - 2400 ksi
Compressive Strength 138 - 152 MPa
20000 - 22000 psi
Izod Impact, Notched 6.41 - 8.54 J/cm
12.0 - 16.0 ft-lb/in
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Dielectric Strength 19.1 kV/mm
486 kV/in
Short Time
Dissipation Factor 0.031

@Frequency 60 Hz
0.031

@Frequency 60 Hz
Condition A
0.055

@Frequency 60 Hz
0.055

@Frequency 60 Hz
Condition D
0.187

@Frequency 60 Hz
0.187

@Frequency 60 Hz
Condition A
0.195

@Frequency 60 Hz
0.195

@Frequency 60 Hz
Condition D
Arc Resistance 185 sec
185 sec
Processing Properties Metric English Comments
Mold Temperature 138 - 166 °C
280 - 330 °F