Dow FLEXOMER™ DFDA-1010 NT 7 Very Low Density Polyethylene (VLDPE) Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Dow Chemical
Trade Name	FLEXOMER™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow FLEXOMER™ DFDA-1010 NT 7 Very Low Density Polyethylene (VLDPE) Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FLEXOMER™ DFDA-1010 NT 7 is an ethylene-butene copolymer produced via gas phase polymerization from Dow. It can be utilized in monolayer and co-extruded films and in blends with other polyolefins to enhance toughness of the structure. Information provided by Dow

Physical Properties	Metric	English	Comments
Density	0.9055 g/cc	0.03271 lb/in³	ASTM D792
High Load Melt Index	20 g/10 min @Load 21.6 kg, Temperature 190 °C	20 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238
Melt Index of Compound	0.85 g/10 min @Load 2.16 kg, Temperature 190 °C	0.85 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	91	91	1 sec; molded and tested in accordance with ASTM D4976; ASTM D2240
	95	95	5 sec; molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break	23.8 MPa	3450 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break	800 %	800 %	Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus	0.152 GPa	22.0 ksi	2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 A

Thermal Properties	Metric	English	Comments
Melting Point	119 °C	246 °F	Dow Method (DSC)
Glass Transition Temp, Tg	-38.9 °C	-38.0 °F	Dow Method