- Dow DOWLEX™ 2045.02 Linear Low Density Polyethylene, Heavy Duty Film Grade
Dow DOWLEX™ 2045.02 Linear Low Density Polyethylene, Heavy Duty Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2045.02 Linear Low Density Polyethylene, Heavy Duty Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOWLEX® 2045.02 Polyethylene resin is a premier film resin for general packaging applications ranging from heavy duty applications to high speed, thin gauge applications. It contains high level of slip additive and medium level of antiblock additive. This resin complies with U.S. FDA regulation 21 CFR 177.1520 (c) 3.2 (a) for food contact applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg |
1.0 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | |
| Film Tensile Strength at Yield, TD | 12.1 MPa | 1750 psi | |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
| Film Elongation at Break, MD | 520 % | 520 % | |
| Film Elongation at Break, TD | 670 % | 670 % | |
| Elongation at Break | 1000 % | 1000 % | Molded value |
| Elmendorf Tear Strength MD | 260 g | 260 g | |
| Elmendorf Tear Strength TD | 640 g | 640 g | |
| Elmendorf Tear Strength, MD | 10.4 g/micron | 264 g/mil | |
| Elmendorf Tear Strength, TD | 25.6 g/micron | 650 g/mil | |
| Dart Drop | 8.40 g/micron | 213 g/mil | |
| Film Tensile Strength at Break, MD | 51.4 MPa | 7450 psi | |
| Film Tensile Strength at Break, TD | 37.2 MPa | 5400 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 106 °C | 223 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % | 10 % | |
| Gloss | 55 % | 55 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 226 °C | 439 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- Dow Pellethane® 2103-90AEF Polyurethane Elastomer, Ether Based (discontinued **)
- Nitriflex N-7 NBR - Nitrile Rubber
- Karina E 550-25/1-AY-IS-BZ Natural PVC Compound
- Teknor Apex Chemlon® 233 GVH Nylon 6, 33% Glass Fiber Reinforced
- Polyplastics Duranex® 2002 Polybutylene Terephthalate (PBT), Standard
- ELASTO UK Dryflex® 5029-104 TPE, Modified Injection Molding Grade for Door Stops
- Chosun Refractories H-3 High Alumina brick
- Eurotec® Tecolen® CP20 MF20 NL XA70 PPCP, 20% mineral filled, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- Arlon 55978X030 0.0305" (0.775 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M SJ6506 Protective Product, Molded Shapes
Copyright © lookpolymers.com All Rights Reserved