ExxonMobil Bicor® 70 HBS-2 OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 70 HBS-2 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor HBS-2 is a one-side sealable, one-side high barrier PVdC-coated OPP film designed for use as the inside sealant web in high-barrier laminations.Availability: Latin America, North America and South AmericaKey Features:Excellent moisture and oxygen barriersExcellent flavor and aroma barrierExcellent sealability, hot tack and seal rangeLap sealable to coex outer webFeatures:Flavor & Aroma BarrierGas BarrierHigh Barrier PVdC CoatedIn Lamination Lap SealableMoisture BarrierOxygen BarrierPVdC CoatedApplications:BakeryBiscuits/Cookie/CrackersBox OverwrapConfectionery, SugarCrisps and SnacksUses:HFF Flexible PackagingPre-made BAgs - Flexible PackagingVFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Printing and Solvent Rotogravure Printing Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 2.50 g/m²/day | 0.161 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 4.70 cc/m²/day | 0.303 cc/100 in²/day | 23°C, 0% RH; ExxonMobil Method |
| Thickness | 17.8 microns | 0.700 mil | Nominal; ExxonMobil Method |
| Coating Weight | 17.4 g/m² | 10.9 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 114 MPa | 16500 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 207 MPa | 30000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.8 % | 1.8 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 195°F | 200g/in |
| Crimp Seal Strength | 430 g/in | 260°F, 20psi, 3/4sec |
| Yield | 39500 in2/lb |
Users viewing this material also viewed the following:
- Nylene® 6111 (HS) , 40% Glass/Mineral Reinforced Nylon 6/6
- LNP Stat-Kon® LC-1003 EM Polyetheretherketone, Carbon Fiber Reinforcement (discontinued **)
- Teknor Apex Monprene® MP-1646-L3 Thermoplastic Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP AW00A ABS (Europe-Africa-Middle East)
- CeramTec CD 101 Silicon Carbide, SiC-ZrB2
- Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, 3K High Strength Carbon
- EMS-Grivory Grivory® LV-3H PA12-GF30
- Daikin POLYFLON MG-6030 PTFE 15% Carbon Fiber Filled Molding Powder
- DuPont Elvaloy® 1126 AC Ethylene and 25% Methyl Acrylate Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved