Diamond Polymers PC 2109T Natural, UV Stabilized, Flame Retardant Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate, UV Stabilized
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Diamond Polymers PC 2109T Natural, UV Stabilized, Flame Retardant Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Water Absorption 0.15 %
<br>@Temperature 23.0 °C,<br> Time 86400 sec
 0.15 %
<br>@Temperature 73.4 °F,<br> Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0070 cm/cm
0.0020 - 0.0070 in/in
ASTM D955
Melt Flow 15 g/10 min
<br>@Load 1.20 kg,<br> Temperature 300 °C
 15 g/10 min
<br>@Load 2.65 lb,<br> Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 61.3 MPa
8890 psi
chs 2.0 in/min; ASTM D638
Flexural Strength 90.1 MPa
13100 psi
chs 0.05 in/min; 5% strain; ASTM D790
Flexural Modulus 2.205 GPa
319.8 ksi
chs 0.05 in/min; ASTM D790
Izod Impact, Notched 7.47 J/cm
<br>@Thickness 3.17 mm
 14.0 ft-lb/in
<br>@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
0.125&quot;;; ASTM D648
Vicat Softening Point 150 °C
<br>@Load 1.00 kg,<br> Thickness 3.17 mm
 302 °F
<br>@Load 2.20 lb,<br> Thickness 0.125 in
 ASTM D1525
Flammability, UL94 V-0
<br>@Thickness 1.57 mm
 V-0
<br>@Thickness 0.0620 in
V-0
<br>@Thickness 3.17 mm
 V-0
<br>@Thickness 0.125 in