Diamond Polymers NPP25-0120B GF15 Glass Filled Copolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Glass Reinforced, Impact Modified |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers NPP25-0120B GF15 Glass Filled Copolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ASTM D955 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.90 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ash | 15 % | 15 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 0.60 % | 0.60 % | chs 2.0 in/min; ASTM D638 |
| Tensile Modulus | 3.007 GPa | 436.1 ksi | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 44.4 MPa @Thickness 3.17 mm |
6440 psi @Thickness 0.125 in |
chs 0.05 in/min; SL 2 inches; ASTM D790 |
| Flexural Modulus | 2.983 GPa @Thickness 3.17 mm |
432.6 ksi @Thickness 0.125 in |
chs 0.05 in/min; SL 2 inches; ASTM D790 |
| Izod Impact, Notched | 1.816 J/cm @Thickness 3.17 mm |
3.402 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | 0.125";; ASTM D648 |
| Vicat Softening Point | 152 °C @Load 1.00 kg |
306 °F @Load 2.20 lb |
120°C/hr; ASTM D1525 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC T4030 E20 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified
- Permabond UV630 UV-curable Adhesive
- SABIC Innovative Plastics LNP Thermocomp GX05053 PSU (Europe-Africa-Middle East)
- Borealis Casico™ FR4804 Non-Halogen Flame Retardant Compound for Low Voltage Insulation and Jacketing
- Cossa Polimeri ESTAPROP H 0360 T8 Polypropylene, 30% Mineral Filled
- Eurostar Starflam AFR200B PA66, Flame Retardant, Injection Molding
- Arkema Group Orevac® 9305 Film EVA-MAH Terpolymer
- 3M 4008 Double Coated Urethane Foam Tape
- Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved