ExxonMobil Escorene® LD 712.06 Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD 712.06 Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Escorene Ultra LD 712 series is a fraction melt index, 10 wt% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughness, particularly at low temperatures.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.931 g/cc
0.0336 lb/in³
ExxonMobil Method
Vinyl Acetate Content 10 %
10 %
ExxonMobil Method
Thickness 52.1 microns
2.05 mil
Melt Flow 0.35 g/10 min
0.35 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.10 MPa
1030 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 6.21 MPa
900 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 360 %
360 %
ASTM D882
Film Elongation at Break, TD 640 %
640 %
ASTM D882
Film Elongation at Yield, MD 8.1 %
8.1 %
ASTM D882
Film Elongation at Yield, TD 6.1 %
6.1 %
ASTM D882
Elmendorf Tear Strength, MD 2.113 g/micron
53.66 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 1.920 g/micron
48.78 g/mil
ASTM D1922
Dart Drop 11.522 g/micron
292.67 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 34.1 MPa
4940 psi
ASTM D882
Film Tensile Strength at Break, TD 34.3 MPa
4970 psi
ASTM D882
1% Secant Modulus, MD 112 MPa
16200 psi
ASTM D882
1% Secant Modulus, TD 126 MPa
18300 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 97.8 °C
208 °F
Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point 83.9 °C
183 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 3.2 %
3.2 %
ASTM D1003
Gloss 80 %
80 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer