- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Diamond Polymers ASA S140
Diamond Polymers ASA S140
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA S140.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Medium ImpactInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 3.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.31 GPa | 335 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 2.08 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
3.90 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.1 °C | 178 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 92.2 °C | 198 °F | 0.125 inch, 1 Kg; ASTM D1525 |
Users viewing this material also viewed the following:
- Lanxess Durethan® BKV 135 DUS008 000000 Nylon 6, 35% Glass Fiber
- SABIC Innovative Plastics ULTEM SF2350 PEI Blend
- Tipco Tipcolite® THR 211 Phenolic Compound, Asbestos Wood Flour & Minerals, Soft Flow & High Electrical Properties
- Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/G803/1200 Fabric
- A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene
- A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET
- A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene
- Axiall 8750 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved