Daikin DAI-EL G-752 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Daikin Industries |
| Trade Name | DAI-EL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daikin DAI-EL G-752 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Information provided by Daikin Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 30 @Temperature 121 °C |
30 @Temperature 250 °F |
ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Peak value, at 25°C |
| Tensile Strength at Break | 14.6 MPa | 2120 psi | |
| Tensile Strength, Yield | 2.40 MPa @Strain 100 % |
348 psi @Strain 100 % |
|
| Elongation at Break | 310 % | 310 % | |
| Tear Strength | 23.5 kN/m | 134 pli | at 25°C |
| Compression Set | 20 % | 20 % | 70 hours at 25°C |
| 11 % @Temperature 100 °C |
11 % @Temperature 212 °F |
70 hours | |
| 16 % @Temperature 175 °C |
16 % @Temperature 347 °F |
70 hours | |
| 27 % @Temperature 200 °C |
27 % @Temperature 392 °F |
70 hours |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -13.0 °C | 8.60 °F | Gehman torsion test, T10 | |
| -9.00 °C | 15.8 °F | TR test, TR70 | |
| -6.00 °C | 21.2 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -24.0 °C | -11.2 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 2.90 min | 0.0483 hour | Curelastmeter |
Users viewing this material also viewed the following:
- Nye Lubricants 570M (NT) Synthetic Oil
- RheTech Products T10P100-01 10% Talc Reinforced Polypropylene, Black
- Ravago Manufacturing Americas Hylex® P1317L Polycarbonate, UV Stabilized, Higher Flow, Mold Release
- Momentive Performance Materials RTV60 Red Extreme High Temperature Potting/Encapsulating Compound
- Saint-Gobain CHR® 2300-5R UHMW Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- Westlake Epolene® E-10 Emulsifiable - Oxidized Low Molecular Weight Polyethylene Polymer
- TIMET 10-2-3 Titanium Alloy (Ti-10V-2Fe-3Al), Aged Billet/Bar per ASTM 4986
- C.O.I.M. LARIPUR® LPR5260 PTMG Polyether Polyurethane
- Abatron AboCast 37-10/AboCure 37-10 Adhesive/Casting
Copyright © lookpolymers.com All Rights Reserved