Daikin DAI-EL G-671 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 67% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-671 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 67% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Excellent low-temperature sealing for O-rings.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.84 g/cc
1.84 g/cc
at 25°C
Mooney Viscosity 35

@Temperature 121 °C
35

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 71
71
Peak value, at 25°C
Tensile Strength at Break 16.0 MPa
2320 psi
Tensile Strength, Yield 5.10 MPa

@Strain 100 %
740 psi

@Strain 100 %
Elongation at Break 210 %
210 %
Tear Strength 20.0 kN/m
114 pli
at 25°C
Compression Set 10 %
10 %
70 hours at 25°C
7.0 %

@Temperature 100 °C
7.0 %

@Temperature 212 °F
70 hours
10 %

@Temperature 175 °C
10 %

@Temperature 347 °F
70 hours
19 %

@Temperature 200 °C
19 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -20.0 °C
-4.00 °F
TR test, TR10
-14.7 °C
5.54 °F
Gehman torsion test, T10
-10.0 °C
14.0 °F
TR test, TR70
-9.00 °C
15.8 °F
Gehman torsion test, T2
Brittleness Temperature -23.0 °C
-9.40 °F
Processing Properties Metric English Comments
Processing Temperature 170 °C
338 °F
Cure Measuring Temperature
Cure Time 3.00 min
0.0500 hour
Curelastmeter