CP-Polymer-Technik Wellamid® 6000 MR 409 HWCP Mineral Nylon 6, Heat Stabilized, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000 MR 409 HWCP Mineral Nylon 6, Heat Stabilized, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.5 - 2.0 % | 1.5 - 2.0 % | 23°C/50%RH, Starting when dry; DIN 53495 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm @Thickness 4.00 mm |
0.0080 - 0.010 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 14 % | 14 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527 |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | Kofler |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | ISO 3915 |
| Dielectric Constant | 6.0 @Frequency 1e+6 Hz |
6.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.20 | 0.20 | At 1 MHz; IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | High | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- Mytex Polymers AS33L-16 Polypropylene, Rubber modified, Talc filled, Compounded
- Solvay Specialty Polymers Algoflon® 20FLCA PTFE; Calcium Fluoride Filled (discontinued **)
- Mearthane Durethaneâ„¢ S DS-720A Solid Polyurethane Elastomer
- Schott DUROBAX® amber Neutral Glass Tubing
- Solvay Specialty Polymers Veradel® 3400 Polyethersulfone (PESU)
- SABIC Innovative Plastics LNP THERMOCOMP RF008S PA 66
- Trelleborg Emerson & Cuming Stycast® 3180M Two-Component Easy Mix Ratio Encapsulant
- Axiall SP-7008 Rigid PVC, Molding
- Arlon Thermabond® R36200A008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Akro-Plastic Akromid® A3 S1 PA, Cold-Impact Resistant (discontinued **)
Copyright © lookpolymers.com All Rights Reserved